The present invention provides one kind of heat conduction abrasion resistant refractory material, which is made up of Magnesium Oxide powder as main raw material, adding dispersant and organic binder, and is formed by grouting. This product is composed of good heat conduction performance of raw materials, the main crystal phase of Magnesium Oxide, the porosity is less than 2%, uniform and compact, has good thermal conductivity, thermal conductivity of 1000 DEG C to 30 ~ 35W/ (m.k), Mohs hardness is slightly higher than that of corundum hardness, have high wear resistance, high temperature resistant performance is good, load softening temperature can reach 1680 DEG C.
【技术实现步骤摘要】
本专利技术属于耐火材料领域,具体涉及一种高导热高耐磨耐火材料。
技术介绍
目前还原炉、焦炉、石油焦煅烧炉等隔焰加热的工业窑炉的主体耐材多选用高铝砖、硅砖等,存在着导热系数低、耐磨性差等问题,导致生产效率低,使用寿命短等问题出现。
技术实现思路
本专利技术的目的在于提供一种导热耐磨耐火材料,该材料导热系数高、耐磨性能好,能够有效改善目前还原炉、焦炉、石油焦煅烧炉等隔焰加热工业窑炉生产效率低,使用寿命短。为了实现以上技术效果,本专利技术提供了一种导热耐磨耐火材料的制备方法,其特征在于,其原料包含以下质量百分比的物质:氧化镁微粉90~95分散剂2.5~5有机结合剂2~5将以上原料混合后注浆成型,在1650~1750℃下烧结完成。本专利技术所提供的导热耐磨耐火材料的制备方法,其原料及重量百分比优选为:氧化镁微粉95分散剂2.8有机结合剂2.2所述烧结温度优选为1750℃。所述分散剂优选为羧甲基丙烯酸铵。所述有机结合剂优选为亚甲基双丙烯酰胺。本专利技术还请求保护根据以上导热耐磨耐火材料的制备方法制备得到的导热耐磨耐火材料。本专利技术所提供的导热耐磨耐火材料由导热性能较好的原材料构成,主要晶相氧化镁,气孔率≤2%,均匀致密,具有较好的导热性,1000℃下导热系数能够达到30~35W/(m.k)左右,莫氏硬度略高于刚玉硬度,具有较高的耐磨性能,耐高温性能好,荷重软化温度能够达到1680℃以上。该耐火材料制品具有较高的导热性能和耐磨性能,其中1000℃导热系数是高铝砖、硅砖的15倍,耐磨性能是高铝砖及硅砖的5倍左右具体实施方式为了使本专利技术技术方案更容易理解,现结合具体实 ...
【技术保护点】
一种导热耐磨耐火材料的制备方法,其特征在于,其原料包含以下质量百分比的物质:氧化镁微粉 90~95分散剂 2.5~5有机结合剂 2~5将以上原料混合,经球磨机预混后,注浆成型,在1650~1750℃下烧结完成。
【技术特征摘要】
1.一种导热耐磨耐火材料的制备方法,其特征在于,其原料包含以下质量百分比的物质:氧化镁微粉90~95分散剂2.5~5有机结合剂2~5将以上原料混合,经球磨机预混后,注浆成型,在1650~1750℃下烧结完成。2.根据权利要求1所述的导热耐磨耐火材料的制备方法,其特征在于,其原料及重量百分比为:氧化镁微粉95分散剂2.8有机结合剂2.2。3.根据权利要求1所述的导热耐磨...
【专利技术属性】
技术研发人员:李建涛,范晓凯,陈泉锋,
申请(专利权)人:郑州安联凯实业有限公司,
类型:发明
国别省市:河南;41