The invention belongs to the technical field of the preparation of functional materials, and relates to a method for high boric acid modified phase emulsion preparation of macroporous polymer adsorbent. The big hole imprinted by a process for high internal phase emulsions free radical polymerization of the invention by affinity adsorbent with boron; after a series of processing by adsorbent, and will be used for natural flavonoids in aqueous solution of luteolin selective recognition and separation; preparation of macroporous adsorbent type high boric acid imprinted polymers prepared by the invention repair a phase emulsion with large specific surface area, adsorption capacity is very large, with good performance and fast response of acid-base adsorption desorption process.
【技术实现步骤摘要】
本专利技术属于环境功能材料制备
，涉及一种硼酸型修饰的高内相乳液制备大孔印迹聚合物吸附剂的方法。
技术介绍
固体物质的表面对于流体都具有一定的物理吸附作用，吸附剂有巨大的内表面积和大的孔隙率，因此受到广泛的关注并且被应用于诸多领域，例如活性炭、活性氧化铝、硅胶和分子筛等等；制备吸附剂的传统方法就是通过聚合以表面活性剂来稳定的高内相乳液来制取，高内相乳液(HighInternalPhaseEmulsion,HIPE)又称高浓乳液，它是一种分散相体积分数大于74.05％的乳液。硼亲和是指硼酸基团和顺式二羟基结构在碱性下结合生成五圆环结构，在酸性条件下发生解离。分子印迹技术是指分子印迹技术是制备具有识别性位点的三维材料。通过功能单体和模版分子的特性行识别来达到需求。分子印迹技术具有很多优势如活性位点嵌入过深，同时吸附动力学速率慢，吸附-解吸附的动力学性能不佳等。木犀草素作为天然黄酮类化合物，具有多种药理活性，如抗菌，抗癌，抗病毒，抗氧化等能力。因此回收它具有很大的意义。因此本工作是乳液自由基聚合的方法制备大孔印迹吸附剂，在高内下乳液中中引入乙烯基硼酸单体然后用来...
【技术保护点】
一种硼酸型修饰的高内相乳液制备大孔印迹聚合物吸附剂的制备方法，其特征在于，按照如下步骤进行：(1)首先将丙烯酸丁酯和EGDMA混合，然后再加入VPBA和AIBN，作为连续相的混合物用超声波均匀分散4‑6min；(2)将步骤(1)得到的混合物在800rpm的恒定搅拌下，向其中加入表面活性剂超级聚合物2296和K2SO4，4‑6min后形成稳定的W/O HIPEs乳液；(3)将步骤(2)所得W/O HIPEs乳液转移到玻璃瓶中，将玻璃模具密封并在60‑80℃的恒温水浴中加热6‑24h，随后，通过在一定数量的丙酮中索氏来纯化所获得的MPs‑BA‑1和MPs‑BA‑0，然后真空烘干。
【技术特征摘要】
1.一种硼酸型修饰的高内相乳液制备大孔印迹聚合物吸附剂的制备方法，其特征在于，按照如下步骤进行：(1)首先将丙烯酸丁酯和EGDMA混合，然后再加入VPBA和AIBN，作为连续相的混合物用超声波均匀分散4-6min；(2)将步骤(1)得到的混合物在800rpm的恒定搅拌下，向其中加入表面活性剂超级聚合物2296和K2SO4，4-6min后形成稳定的W/OHIPEs乳液；(3)将步骤(2)所得W/OHIPEs乳液转移到玻璃瓶中，将玻璃模具密封并在60-80℃的恒温水浴中加热6-24h，随后，通过在一定数量的丙酮中索氏来纯化所获得的MP...
【专利技术属性】
技术研发人员：刘树成，潘建明，王晓静，吴润润，
申请(专利权)人：江苏大学，
类型：发明