The present invention discloses a flame retardant wear resistant PE plastic pipe, which is composed of the following parts by weight of raw materials: high density polyethylene 70 78, ethylene octene block copolymer 18 24 copies, 20 copies of the ancient Malone resin 15 silica, 5 9 copies, 14 copies, 12 yellow phthalate two two 4 9 a formic acid anhydride, silane coupling agent KH5600 6 10 copies, 25 copies of the 20 epoxy resin, bentonite 10 15 phosphite three phenyl 5 9. The flame retardant wear-resisting PE plastic pipe provided by the invention has good flame retardant performance and high heat resistance, good compatibility, improved mechanical properties of the composite material, high density, high compressive strength, good abrasion resistance.
【技术实现步骤摘要】
本专利技术属于高分子材料领域,具体涉及一种阻燃耐磨PE塑料管材。
技术介绍
聚乙烯(polyethylene,简称PE)是乙烯经聚合制得的一种热塑性树脂。聚乙烯依聚合方法、分子量高低、链结构之不同,分高密度聚乙烯、低密度聚乙烯及线性低密度聚乙烯。其中高密度聚乙烯(HIGHDENSITYPOLYETHYLENE,HDPE)俗称低压聚乙烯,与LDPE及LLDPE相较,有较高之耐温、耐油性、耐蒸汽渗透性及抗环境应力开裂性,此外电绝缘性和抗冲击性及耐寒性能很好,主要应用于吹塑、注塑等领域。由高密度聚乙烯制成的HDPE管材是传统的钢铁管材、聚氯乙烯管材的换代产品,它主要承担雨水、污水、农田排灌等排水的任务,广泛用于公路、铁路路基、地铁工程、废弃物填埋场、隧道、绿化带、运动场及含水量偏高引起的边坡防护等排水领域,以及农业、园艺之地下灌溉、排水系统。而目前市场上的HDPE管材存在着易燃,离火后能继续燃烧,表面硬度低,易刮伤的缺点,极大限制了HDPE管的使用,为此,我们从产品的配方着手,开发新的高性能的HDPE管材,提供一种阻燃耐磨PE塑料管材。
技术实现思路
本专利技术的目的在于提供一种阻燃耐磨PE塑料管材。为了实现上述目的,本专利技术提供了一种阻燃耐磨PE塑料管材,由以下重量份的原料制得:高密度聚乙烯70-78份、乙烯-辛烯嵌段型共聚物18-24份、古马隆树脂15-20份、二氧化硅5-9份、黄丹12-14份、邻苯二甲酸二甲酐4-9份、硅烷偶联剂KH56006-10份、环氧树脂20-25份、膨润土10-15份、亚磷酸三苯酯5-9份。其还包含月桂醇硫酸钠3-5份。其还包含乙 ...
【技术保护点】
一种阻燃耐磨PE塑料管材,其特征在于:由以下重量份的原料制成:高密度聚乙烯70‑78份、乙烯‑辛烯嵌段型共聚物18‑24份、古马隆树脂15‑20份、二氧化硅5‑9份、黄丹12‑14份、邻苯二甲酸二甲酐4‑9份、硅烷偶联剂KH5600 6‑10份、环氧树脂20‑25份、膨润土10‑15份、亚磷酸三苯酯5‑9份。
【技术特征摘要】
1.一种阻燃耐磨PE塑料管材,其特征在于:由以下重量份的原料制成:高密度聚乙烯70-78份、乙烯-辛烯嵌段型共聚物18-24份、古马隆树脂15-20份、二氧化硅5-9份、黄丹12-14份、邻苯二甲酸二甲酐4-9份、硅烷偶联剂KH56006-10份、环氧树脂20-25份、膨润土10-15份、亚磷酸...