一种抗冲击防穿甲用材、及其制备方法技术

本发明专利技术提供一种抗冲击防穿甲用材、及其制备方法，该种材料的制备方法为先将各原料按重量配伍进行均质化处理，然后燥干、研磨；本发明专利技术的抗冲击防穿甲用材具有质量轻、高刚度、抗冲击、缓震效果好等优点，尤其是在抗冲击、缓震方面的性能优异，研产成本低、实施无污染、工艺简约，可用于制作抗冲击防穿甲、以及防护用材，对于保护人居环境、促进经济社会的可持续发展或许具有重要的意义。

Impact resistant armor proof material and preparation method thereof

The invention provides a shock resistant armor material, and its preparation method, the material preparation method for combining homogenization treatment the raw materials by weight and then dried, and grinding; anti shock anti armor material has the advantages of light weight, high rigidity, shock resistance, good cushioning effect the advantages of the present invention, especially in the anti impact and corrosion properties of the excellent shock, research and production low cost, no pollution, simple implementation process, can be used for the production of anti armor and anti impact protection material, has important significance for the protection of the living environment, promote sustainable economic and social development or a.

【技术实现步骤摘要】

本专利技术属于复合材料
，特别涉及一种抗冲击防穿甲用材、及其制备方法。技术背景一直以来，在社会生产以及民生建设活动中，对于使用的工具，抗冲击、耐磨擦，谋求安全性，是一个重要的课题。突破原始的分层设计，立体化、简约化考虑，通过千方百计改变材料的组分，使其成为新的一体功能性材料。例如，通常所用的防冲击、避割、耐磨、以及特种韧固工具等，概由不同的合金、玻璃纤维和碳纤维，通过不同的排列位置和交错层次产生、设计成板面一般都是在这些基础上分层设计或采取多元方式成型的。若要基材性能整体性地提升，尝试在配伍材料中添加无机体，形成复合材料，无机粉体或晶须或层片对抗冲击性、缓震性、以及降低材料熔点等方面的提高有很大的贡献。同时，为解决生产成本高，工艺多元，并且材料的耐温性、抗老性、耐腐蚀性差，和正性力学性能的改善、甚或提升，以满足社会生产、及民生应用的要求，本专利技术研究设计者开发新的高性能的复合材料，拟提供一种抗冲击防穿甲用材、及其制备方法，其设计生产研产成本低，实施无环保污染，为解决现有问题，对于保护人居环境、促进经济社会的可持续发展或许具有重要的意义。
技术实现思路
基于上述现状，本专利技本文档来自技高网...

【技术保护点】
一种抗冲击防穿甲用材、及其制备方法，其特征在于，所用基材包括：按重量份配伍：硅钛合金粉55‑65份、低苯硅橡胶15‑20份、芳纶纤维10‑15份、PEHR4‑5份、表面改性剂硅酸钠2‑3份、硅酸铝纤维素5‑10份。

【技术特征摘要】
1.一种抗冲击防穿甲用材、及其制备方法，其特征在于，所用基材包括：按重量份配伍：硅钛合金粉55-65份、低苯硅橡胶15-20份、芳纶纤维10-15份、PEHR4-5份、...