The invention provides a preparation method of building thermal insulation material, which comprises glass cotton, perlite, attapulgite, silica, sodium fluosilicate and aluminum dihydrogen phosphate. The material is put into the reactor and stirred to form slurry, and then spray the fireproof agent (silica sol) to the rubber powder particles. The invention has the advantages of low thermal conductivity, good heat insulation effect, small bulk density, high safety strength, difficulty in producing dust during manufacture, and good non combustibility. It is green, environmental friendly, and can adapt to more complex building structures.
【技术实现步骤摘要】
一种建筑保温材料的制备方法
本专利技术属于保温材料的
,具体涉及一种建筑保温材料的制备方法。
技术介绍
随着经济的发展,墙体保温材料的发展也是在不断的完善,发展初期针对保温性能比较重视,在短短的十几年时间里得到了广泛应用和普及。随着材料的不断更新完善,现阶段主要以保温、安全、环保为主题。目前,市场上建筑方面的保温材料比较常用的是水泥、加气混凝土、酚醛泡沫保温板、玻璃棉板等。其中,水泥、加气混凝土的不足之处是容重比较大,收缩大,干缩变形和温度变形比较大,导热系数较大。与砂浆的粘结性差,由于加气混凝土砌块的吸水性强,因此容易将砂浆中的水分夺走,导致砂浆粘结性变差、水化不良,导致粉刷层空鼓等。酚醛泡沫保温板具有优异的防火性能,优良的绝热性能,抗腐蚀抗老化,密度小、重量轻,环保。缺点是成本高,价格高,为增加其抗压、抗拉强度,一般会在双面贴一层无机板或网格布。高温下不能使用,不能超过200℃,超过了会有剧毒的烟气,理论上成会抗高温歧变。不耐老化,紫外线等射线长期作用,酚醛保温板会丧失其功能和缩短寿命。生产过程中苯酚和甲醛的生产都是高污染项目。岩棉板具有抗拉强度小,板缝处应力较低,不易出现裂缝的特点。缺点是强度低,吸水率较高,易收缩、开裂,和外保温系统中的各种材料很难配套、相容,系统容易发生开裂、渗漏甚至脱落等质量通病,难于作到与建筑物同寿命。基于以上因素,需要制备一种导热系数低,容重小,安全,绿色,环保的新型保温材料。
技术实现思路
本专利技术提供一种建筑保温材料的制备方法,含有:玻璃棉、珍珠岩、凹凸棒、二氧化硅、氟硅酸钠、双氢磷酸铝。将上述材料放入反应釜中搅拌合 ...
【技术保护点】
一种建筑保温材料的制备方法其特征在于含有:玻璃棉10‑20份、珍珠岩10‑20份、凹凸棒20‑25份、二氧化硅10‑20份、氟硅酸钠4‑8份、双氢磷酸铝2‑5份,在反应釜中搅拌形成浆料,制成胶粉颗粒,再向胶粉颗粒喷洒防火剂。
【技术特征摘要】
1.一种建筑保温材料的制备方法其特征在于含有:玻璃棉10-20份、珍珠岩10-20份、凹凸棒20-25份、二氧化硅10-20份、氟硅酸钠4-8份、双氢磷酸...
【专利技术属性】
技术研发人员:王胜利,
申请(专利权)人:洛阳鼎威材料科技有限公司,
类型:发明
国别省市:河南,41