The invention provides a nano rare earth oxide / polypropylene composite material and a preparation method thereof. The weight of raw materials and raw materials it is: PP 100, 1 to 10 nanometer rare earth oxides, silane coupling agent 0.01 ~ 0.2, 0 ~ 6 additives, nano rare earth oxide which is a mixture of a or several kinds of nano neodymium oxide, cerium oxide, europium oxide, nano nano nano lanthanum oxide, yttrium oxide, samarium oxide and the mixture of the additive is one or several toughening agent, lubricant, nucleating agent and antioxidant. The composite material of the invention has excellent processing performance and is endowed with special optical and electromagnetic properties of rare earth oxides.
【技术实现步骤摘要】
本专利技术属于聚丙烯复合材料领域,具体涉及一种纳米稀土氧化物/聚丙烯复合材料,并涉及一种纳米稀土氧化物/聚丙烯复合材料的制备方法。
技术介绍
聚丙烯是一种通用热塑性塑料,具有优良的力学性能,但在实际使用过程中,考虑到成本或需要赋予其特殊的性能,聚丙烯中一般加入填充料制成复合材料,复合材料的综合力学性能优良,同时也可以降低成本。稀土材料具有优良的光、电、磁等特殊性能,稀土尤其是稀土氧化物在石油、化工、冶金、纺织、陶瓷、玻璃、永磁材料等领域都得到了广泛的应用,随着科技的进步和应用技术的不断突破,稀土氧化物的价值将越来越大。稀土氧化物纳米化后可以凸显稀土材料的特殊光电磁特性,将其填充于聚丙烯复合材料中将赋予聚丙烯特殊的稀土特性,应用前景较好。
技术实现思路
本专利技术的目的在于提供一种纳米稀土氧化物/聚丙烯复合材料,该复合材料加工性能优良,并被赋予稀土氧化物的特殊光电磁性能。本专利技术还提供一种纳米稀土氧化物/聚丙烯复合材料的制备方法。本专利技术采用的技术方案为:一种纳米稀土氧化物/聚丙烯复合材料及其制备方法,其特征在于,它的原料及原料的重量份数为:聚丙烯100份,纳米稀土氧化物1~10份,硅烷偶联剂0.01~0.2份,助剂0~6份,所述制备方法包括如下步骤:(1)采用硅烷偶联剂对纳米稀土氧化物进行表面处理;(2)准确称量聚丙烯和各种助剂,连同表面处理的纳米稀土氧化物加入高速混合机内,充分混合,得到混合料;(3)将混合料采用双螺杆 ...
【技术保护点】
一种纳米稀土氧化物/聚丙烯复合材料及其制备方法,其特征在于,它的原料及原料的重量份数为:聚丙烯 100份,纳米稀土氧化物 1~10份,硅烷偶联剂 0.01~0.2份,助剂 0~6份,所述制备方法包括如下步骤:(1)采用硅烷偶联剂对纳米稀土氧化物进行表面处理;(2)准确称量聚丙烯和各种助剂,连同表面处理的纳米稀土氧化物加入高速混合机内,充分混合,得到混合料;(3)将混合料采用双螺杆挤出机熔融挤出造粒,制得纳米稀土氧化物/聚丙烯复合材料粒料。
【技术特征摘要】
1.一种纳米稀土氧化物/聚丙烯复合材料及其制备方法,其特征在于,它的原料及原料的重量份数为:
聚丙烯100份,
纳米稀土氧化物1~10份,
硅烷偶联剂0.01~0.2份,
助剂0~6份,
所述制备方法包括如下步骤:
(1)采用硅烷偶联剂对纳米稀土氧化物进行表面处理;
(2)准确称量聚丙烯和各种助剂,连同表面处理的纳米稀土氧化物加入高速混合机内,充分混合,得到混合料;
(3)将混合料采用双...
【专利技术属性】
技术研发人员:王启庸,
申请(专利权)人:天津滨浦生产力促进有限公司,
类型:发明
国别省市:天津;12