Preparation method of sintered ceramic, the invention relates to a ceramic material processing field, firstly, raw material pretreatment, the pretreatment of the raw material by vacuum pressure in vacuum extruder extrusion into a hollow tube compacting, the cutting mechanism and cutting into the hollow diameter close to the length, in the cutting process at the same time both ends closed, into the granulator forming irregular hollow sphere, after sintering and sintering of ceramic pottery. The invention has the advantages of wide raw material sources, easy production process control, high product quality and low cost, and can produce high strength sintered ceramsite with higher strength than clay ceramsite and small density.
【技术实现步骤摘要】
本专利技术涉及陶瓷材料加工领城,特别是一种烧结陶粒的生产方法。
技术介绍
传统制造烧胀陶粒(以下通称陶粒)是利用黏土、页岩或粉煤灰等可烧胀原料加水搅拌、成球,通过回转窑在高温下,利用可烧胀原料在高温下膨胀的特性经膨化而形成中空的球体或球柱状球体,多呈不规则的次圆状、次棱角状,冷却后就是陶粒。生产的原料必须是可烧胀原料,而这种原料在自然界很少,因此需要用添加剂来改善其膨胀特性,由于粘土、页岩等原料性能千差万别,即使一批原料性能差异也很大,添加剂既增加成本又很难稳定加入,对产品质量造成很大影响,这种方法还极大地浪费了土地资源,而且有相当一部分地域的粘土、页岩等根本不能烧胀或在高温烧结后收缩,即使加上添加剂也无法膨胀来制造陶粒,这使得陶粒的制造存在原料上的局限性;再一方面陶粒的生产过程是在高温下膨化而形成中空的球体,能耗较高、成本高;由原料性能来保证产品性能和产品尺寸,工艺很难控制,为了解决这一问题,烧胀后进行筛分,一般粒径大的为陶粒,粒径小的为陶砂,比例也无法控制。
技术实现思路
本专利技术的目的是提供一种原料来源广泛、生产工艺容易控制、产品质量高、成本低廉的。本专利技术是,首先对原材料进行预处理,将经预处理的原料由真空挤出机在真空状态下高压挤出成密实的中空管,再由切削机构切削成和中空管直径接近的长度,在切削过程中同时将两端封闭后,进入造粒机形成中空的不规则球体,后经烧结陶化而成烧结陶粒。烧结陶粒用材料采用煤矸石,或者瘠土,或者河泥,或者煤粉,或者炉渣,或者粉煤灰,或者煤矸石,或者以上任一两种或两种以上的材料组合,烧结而成。本专利技术的原料来源广泛,生产工艺容 ...
【技术保护点】
烧结陶粒的制备方法,首先对原材料进行预处理,其特征在于将经预处理的原料由真空挤出机在真空状态下高压挤出成密实的中空管,再由切削机构切削成和中空管直径接近的长度,在切削过程中同时将两端封闭后,进入造粒机形成中空的不规则球体,后经烧结陶化而成烧结陶粒。
【技术特征摘要】
【专利技术属性】
技术研发人员:张殿平,姬广庆,康兴民,
申请(专利权)人:兰州理工大学,
类型:发明
国别省市:62[中国|甘肃]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。