The invention is about the improvement of the ceramic roller, in particular to a high mechanical strength, impact resistance, resistance to temperature shock resistance and abrasion resistance, but not only for hot rolled steel plate transfer roller ceramic, which is characterized by 80 ~ 90 and ceramic fused silica particles aggregate, and from 10 to 20 matrix binder composition. The ceramic roller burning not only has high mechanical and anti impact strength, flexural strength of P and 45MPa; and the expansion coefficient is small, < 0.8 * 10 = 6 / - / C, with excellent resistance to thermal shock temperature of 1000 ~ 30 DEG C water repeatedly 15 times without cracking. And the hardness of roll surface ceramic, abrasion resistance, low running resistance, low friction coefficient, long service life, smooth surface, after grinding surface roughness can be close to 1.6 or even lower, and the steel plate (pressure 10kg / cm = 2) friction 100 times, formed no scratches the surface of the steel plate, a to ensure the surface quality of steel plate.
【技术实现步骤摘要】
本专利技术是关于对陶瓷传送辊的改进，尤其涉及一种机械强度高、抗冲击性强，耐温急变性和耐磨损性好，可用于但不是唯一热轧钢板传送的陶瓷辊。
技术介绍
钢铁厂热轧薄板(如汽车钢板)生产，高温(800℃～900℃)热钢板流转到下一工序，途中均采用辊子平移传送。现钢铁厂传送辊子大都采用铸铁辊，然而铸铁辊在传送钢板时，铁——铁转动磨擦大，不仅造成辊子磨损较大，使用寿命短，增加生产成本，而且磨擦还会造成钢板表面容易生产擦痕，影响板材表面质量。虽然现有技术有用陶瓷辊子作搬运辊传送热产品，然而不同的陶瓷配方，只能用于设计特定要求，不具有通用性。例如辊道窑中使用的陶瓷辊，虽是在高温环境中工作，但工作温度相对稳定，所以对耐急冷急热性要求不高，而且承载产品质量轻，辊子尺寸相对较小，对抗冲击性能及机械强度要求较低，其材质不适用于高温热钢板的传送。再如中国专利95220340.5公开的用于高速线材精轧机复合陶瓷辊环，虽然报导具有较好的耐磨性能和良好的抗热疲劳强度，及较好的抗压强度和抗弯强度，但需采用碳化钨基与氧化铝、氧化锆、钴、氧化镁、钼混合冷压成型、热压烧结，或采用氮化硅基与碳化钛、氧...
【技术保护点】
一种热轧钢板传送用陶瓷辊，其特征是陶瓷辊由８０～９０份熔融石英颗粒骨料，和１０～２０份基质结合料组成。
【技术特征摘要】
【专利技术属性】
技术研发人员：汪伯川，何卫平，冯家迪，
申请(专利权)人：江苏省宜兴非金属化工机械厂，
类型：发明
国别省市：32[中国|江苏]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。