一种多孔莫来石陶瓷材料的制备方法技术

本发明专利技术涉及多孔莫来石陶瓷材料及其制备方法，所采用的技术方案是：按重量百分含量将１０～５０％的煤矸石粉、５０～９０％的Ａｌ（ＯＨ）↓［３］粉进行配料，外加上述混合料重量的２～１０％的水及０～１０％的添加剂，经搅拌、成型，再将成型坯体在１１０℃下干燥４～２４小时，然后在１４００～１６００℃温度下烧成，保温１～８小时。本发明专利技术制备的产品化学成分主要是ＳｉＯ↓［２］与Ａｌ↓［２］Ｏ↓［３］，其主晶相为莫来石或莫来石－刚玉。它是一种气孔率高（３８％～６５％）、平均孔径小（１００ｎｍ～１５μｍ）、气孔分布均匀、强度高的轻质保温耐火材料。

Method for preparing porous mullite ceramic material

The present invention relates to porous mullite ceramic material and its preparation method, the technical proposal is: according to the weight percentage of 10 to 50% of the coal gangue powder, 50 ~ 90% Al (OH) ingredients: 3 powder, and the mixture weight 2 ~ 10% and 0 ~ water 10% additives, stirring, molding, and molded bodies at 110 deg.c for 4 to 24 hours, and then in the 1400 to 1600 DEG C sintering temperature, holding for 1 ~ 8 hours. The chemical composition of the product prepared by the invention is mainly SiO: 2 and Al: 2 O: 3, its main crystalline phases of mullite or mullite corundum. It is a lightweight insulating refractory with high porosity (38% ~ 65%), small average pore diameter (100nm to 15 mu m), uniform pore distribution and high strength.

【技术实现步骤摘要】

本专利技术属于多孔陶瓷材料领域。尤其涉及一种以莫来石、刚玉为主要相成分的轻质保温耐火材料及其制备方法。
技术介绍
目前的保温材料大都属于Al2O3-SiO2系材料(王维邦.耐火材料工艺学.冶金工业出版社，2003)，主要物相为刚玉、莫来石、石英物相与玻璃相。这些保温材料孔径较大，且孔分布不均匀。从造孔工艺角度看，目前制备多孔陶瓷材料及轻质保温耐火材料的方法主要有两种1、加入可燃物法在陶瓷或耐火材料粉料中加入可燃物，如锯末、煤粉、焦碳粉，发泡聚苯乙烯球等，经成型、烧成后，可燃物烧去在材料中形成气孔。如“轻质莫来石砖的研制与应用”(《陶瓷工程》，2002，12)技术，以莫来石熟料、工业氧化铝、高岭土为原料，以锯末屑、泡沫聚苯乙烯珠粒为添加剂，制备了轻质莫来石砖。这种方法的缺点是当可燃物烧不尽时，易在材料中形成“黑芯”；可燃物粉在粉料中易团聚，造成材料内气孔大小不均、气孔分布不均等缺点，加入可燃物粉的量收到限制，不可制备出气孔率很高的材料。2、泡沫法将陶瓷或耐火材料粉制成泥浆，在泥浆中加松香皂等发泡剂与固化剂经搅拌使在泥浆中形成气泡。泥浆经浇注成型、固化与烧结后即得到多孔陶瓷材料。如“本文档来自技高网...

【技术保护点】
一种多孔莫来石陶瓷材料及其制备方法，其特征在于按重量百分含量将１０～５０％的煤矸石粉、５０～９０％的Ａｌ（ＯＨ）↓［３］粉进行配料，外加上述混合料重量的２～１０％的水及０～１０％的添加剂，经搅拌、成型，成型坯体在１１０℃下干燥４～２４小时，然后在１４００～１６００℃温度下烧成，保温１～８小时。

【技术特征摘要】

【专利技术属性】
技术研发人员：李楠，鄢文，李淑静，
申请(专利权)人：武汉科技大学，
类型：发明
国别省市：83[中国|武汉]