一种冰晶玉质全透抛光砖高白透明料配方及产品生产方法组成比例

本发明专利技术公开一种冰晶玉质全透装饰工艺瓷质玻化砖的高白透明料配方及该砖的生产方法。高白透明料配方为：白石粉１０－２５、潮州砂１５－３０、广西砂１５－３０、白玉石粉５－２５、湖南石粉１５－３０、高岭上１０－２０、黑泥１－１０、Ｍ型熔剂０－１０。用该配方经配料、球磨、混色、喷雾干燥、成型、干燥、烧成、抛光可制得具有冰晶玉质透明感、超高白度，高光泽度，无辐射无放射性污染、无针孔、无熔洞、无有机物、耐磨防滑、具有较高膨胀系数的瓷砖。

A crystal full through the production of high white transparent material formulation and product polishing brick

High white transparent material formula of the invention discloses a crystal transparent decorative porcelain brick and production method of the brick. High white transparent material formula: white stone powder is 10 - 25, 15 - 30, Guangxi Chaozhou sand sand of 15 - 30, 5 - 25, Hunan white powder powder of 15 - 30, 10 - 20, Gaoling black mud 1 - 10, 0 - 10 M flux. The formula of mixing, milling, mixing, spray drying, forming, drying, sintering, polishing can be prepared with crystal transparent, high whiteness, high gloss, no radiation, no radioactive contamination, no pinhole, no weld hole, no organic matter, and has high wear non slip tile expansion coefficient the.

【技术实现步骤摘要】

本专利技术涉及一种冰晶玉质全透装饰工艺瓷质玻化砖的高白透明料配方及该砖的生产方法。
技术介绍
随着抛光砖技术水平不断进步，透明料在抛光砖中的应用范围也不断扩大。普通聚晶微粉也就是含透明料微粉的生产技术已相对成熟，大大小小厂家相继推出一些产品。通常，透明料在聚晶微粉中比例约为25-50％，如进一步提高透明料比例，如达到95％以上就会产生变形大(尤其是后期变形)、针孔熔洞多，透明料白度低(只有45度左右)、发色敏感、色差大、产量低等缺陷。这些难题限制了透明料在微粉抛光砖中的应用，尤其是高白度透明料在抛光砖中的应用。
技术实现思路
本专利技术的目的是克服现有技术的不足，突破性引进了一种冰晶玉质全透抛光砖高白透明料配方及用该配方生产一种冰晶玉质全透装饰工艺瓷质玻化砖的生产方法。为实现上述目的，本专利技术提供的的高白透明料配方为白石粉10-25潮州砂15-30 广西砂15-30 白玉石粉5-25湖南石粉15-30 高岭土10-20 黑泥1-10 M型熔剂0-10。所述的白玉石粉是一种高白、高钾、低温经人工精选破碎至10目以下，多次循环除铁的石粉，其化学组成如下 所述本文档来自技高网...

【技术保护点】
一种冰晶玉质全透抛光砖高白透明料配方，其特征在于：该配方的组分为：白石粉１０－２５潮州砂１５－３０广西砂１５－３０白玉石粉５－２５湖南石粉１５－３０高岭土１０－２０黑泥１－１０Ｍ型熔剂０－１０。

【技术特征摘要】

【专利技术属性】
技术研发人员：关伟华，
申请(专利权)人：关润启，
类型：发明
国别省市：44[中国|广东]