The invention belongs to the building decoration molding material, in particular to a vermiculite composite injection molding material. A pressurized vermiculite composite material, which is characterized by its formula (vermiculite expanded vermiculite) 80%, 5% short glass fibre, synthetic rubber (thermosetting resin) 14%, curing agent 1%; production material proportioning and mixing evenly, extrusion die, at 15 to 20 DEG C at room temperature, 4 ~ 8 hours out of the mold; 40 ~ 60 DEG C at room temperature, 2 ~ 3 hours out of the mold is finished, can also be used in continuous rolling heating molding machine. The building shape made by the invention has similar appearance, weight, processing technique and firmness, and is similar to wood. The utility model is not inflammable in the fire, and can not be penetrated in the water for 48 hours.
【技术实现步骤摘要】
本专利技术属于建筑装饰造型材料，特别特别一种蛭石复合注压型材料。
技术介绍
目前，建筑装饰造型材料有水泥、白水泥、石膏、木材和玻璃钢。这些材料都有其不足之处，如水泥、石膏因本人身比重大。易碎，所以造型不能过细，用木材和玻璃钢造型成本太高，且不能防火。多年来。人们渴望解决这一问题，努力探索新的建筑造型材料，但因限于传统作法，没有找到合适的替代材料。由于村料的限制，致使一些建筑物呆板，缺乏风格。
技术实现思路
本发是为了弥补现有技术的不足，提供了一种成本低、可塑性强的蛭石复合注压型材料。本专利技术是通过如下技术方案实现的一种蛭石复合注压型材料，其特殊之处在于其配方由蛭石(烧胀蛭石)80％，玻璃纤维短丝5％，合成胶(热固性树脂胶)14％，固化剂，1％组成；生产时材料按配比搅拌均匀后，可挤压装模，在15～20℃的室温下，4～8小时出模40～60℃的室温下，2～3小时出模出模即得成品，也可以用机械连续滚压加温成型。本专利技术是一种新旧换代的复合材料，它与现有的建筑造型材料相比具有以下优点1.用本专利技术制作的建筑造型，其外观、比重、加工工艺、坚固程度都和木材相似，将其放在火中不易然，放在水中48小时不渗透、不变型。2.用本专利技术制做中欧式建筑雕塑时，可模压成型，也可直接塑型。3.本专利技术可以代替木材制做家俱门窗或其它美术工艺品等，加工时可用木工工具，锯、刨、凿孔钉钉子建筑胶粘摇均可，4.用本专利技术制做的成品适应各种油漆和和涂料。具体实施方式本专利技术的特征在于配方和生产工艺，其配方为；蛭石(烧胀蛭石)80％，玻璃纤维短丝5％，合成胶(热固性树脂胶)14％，固化剂...
【技术保护点】
一种蛭石复合注压型材料，其特征是：其配方由蛭石（烧胀蛭石）８０％，玻璃纤维短丝５％，合成胶（热固性树脂胶）１４％，固化剂，１％组成；生产时材料按配比搅拌均匀后，可挤压装模，在１５～２０℃的室温下，４～８小时出模；４０～６０℃的室温下，２～３小时出模出模即得成品，也可以用机械连续滚压加温成型。
【技术特征摘要】