The invention discloses a dry glaze for an antique brick. The dry weight of the glaze is composed of the following raw materials by ball milling, spray pulverization after sieving prepared: potassium feldspar 20 - 40, 0 - 15, quartz 5 burnt talc 15 copies, 5 copies of Zinc Oxide, calcite - 10 0 - 5, 10 - 15 ball clay and alumina 5 - 10 5 - 15, barium carbonate, calcined kaolin 5 - 15, 0.2 - 0.5 carboxymethyl cellulose, sodium tripolyphosphate 0.3 - 0.6 copies, 70 copies of water. The dry glaze is bright and colorful, and when pressed, it is pressed and formed in the concave convex surface cloth, the dry glaze, the billet and the glaze, so that the glaze can be uniformly applied and the transition is natural.
【技术实现步骤摘要】
本专利技术涉及无机硅酸盐
，具体地说，是一种仿古砖用干釉料。
技术介绍
通常，釉是一种通过水、颜料、粘结剂和釉基础配方制得的具有高强度和高粘度的材料。它能使陶瓷产品具有丰富的色彩，美丽的外观而深受市场的欢迎。但目前还存在着在凹凸坯面施釉，过渡不自然、着色不均匀的问题。这一技术难题并没有得到有效的解决。
技术实现思路
本专利技术的目的在于，提供一种仿古砖用干釉料。为了实现上述的专利技术目的，本专利技术的技术方案是由下列重量份的原料经球磨研磨，喷雾制粉后过筛制得钾长石20-40份、石英0-15份、烧滑石5-15份、方解石5-10份、氧化锌0-5份、球土10-15份、氧化铝5-10份、碳酸钡5-15份、烧高岭土5-15份、羧甲基纤维素0.2-0.5份、三聚磷酸钠0.3-0.6份、水70份。原料中，还可含有1-5重量份的釉用色料。钾长石的作用是引入K2O、Al2O3和SiO2，是釉的基本成份；石英的作用是引入SiO2，是釉的基本成份；烧滑石可用于釉料的增白；方解石为熔剂，与ZnO、BaCO3形成Ca、Zn、Ba复合无光剂；氧化锌为熔剂和无光剂；球土可给予釉粘性和强度；...
【技术保护点】
一种仿古砖用干釉料，其特征在于，由下列重量份的原料经球磨研磨，喷雾制粉后过筛制得：钾长石２０－４０份、石英０－１５份、烧滑石５－１５份、方解石５－１０份、氧化锌０－５份、球土１０－１５份、氧化铝５－１０份、碳酸钡５－１５份、烧高岭土５－１５份、羧甲基纤维素０．２－０．５份、三聚磷酸钠０．３－０．６份、水７０份。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。