一种超白抛光砖及其生产方法技术

一种超白抛光砖及其生产方法，其特别之处在于是以ＭｇＯ的铝硅酸盐为主晶相的陶瓷，成分由ＭｇＯ、Ａｌ↓［２］Ｏ↓［３］、ＳｉＯ↓［２］、及陶瓷粉料中常见的杂质组成，其中ＭｇＯ的含量为１５－２０％，Ａｌ↓［２］Ｏ↓［３］的含量为８－１２％，ＳｉＯ↓［２］的含量为５５－７０％。本发明专利技术与已有技术相比，所获得的抛光砖具有无须添加任何增白剂的白度达７５度以上的、质感细腻的优点，由于无须增白剂，因此具有环保的优点。

Super white polished brick and production method thereof

A super white polishing brick and its production method, which is aluminum silicate MgO the main crystalline phase of ceramic components by MgO, Al: 2 O: 3, SiO: 2, and ceramic powder in common impurity composition, in which the content of MgO is 15 20%, the content of Al: 2 O: 3 for 812%, 2 SiO: the content for 5570%. Compared with the prior art, the polished brick has the advantages that the whiteness of the polishing brick is above 75 degrees without adding any whitening agent, and the texture is exquisite. Because the whitening brick does not need whitening agent, the polished brick has the advantages of environmental protection.

【技术实现步骤摘要】

本专利技术涉及一种瓷砖及其生产方法。
技术介绍
现有的超白砖一般都是利用传统的K2O-Al2O3-SiO2三元系统结构，再加以一定量的硅酸锆制得的，白度一般在60度左右，且质感方面不理想，达不到天然石材的质感效果。
技术实现思路
本专利技术的专利技术目的在于提供一种无须添加任何增白剂的白度达75度以上的、质感细腻的超白抛光砖及其生产方法。本专利技术的超白抛光砖是这样实现的，是以MgO的铝硅酸盐为主晶相的陶瓷，成分由MgO、Al2O3、SiO2、及陶瓷粉料中常见的杂质组成，其中MgO的含量为15-20％，Al2O3的含量为8-12％，SiO2的含量为55-70％。本专利技术的超白抛光砖的生产方法是这样实现的，以超白石粉、长石为原料，经过粉料的制作过程、压机的压制成型、干燥、烧制、抛光而成，其中超白石粉的用量为60-70重量份，长石粉用量为10-20重量份，超白石粉、长石粉的百分比的成分含量如表所示 由于MgO含量高的配方的烧成范围比较窄，在烧制过程中容易出现变形及针孔缺陷，特在配方中引入适量的长石，以使配方在大大低于共熔温度下提前烧结，以有利于扩大烧结范围，从而有效控制变形及本文档来自技高网...

【技术保护点】
一种超白抛光砖，其特征在于是以ＭｇＯ的铝硅酸盐为主晶相的陶瓷，成分由ＭｇＯ、Ａｌ↓［２］Ｏ↓［３］、ＳｉＯ↓［２］、及陶瓷粉料中常见的杂质组成，其中ＭｇＯ的含量为１５－２０％，Ａｌ↓［２］Ｏ↓［３］的含量为８－１２％，ＳｉＯ↓［２］的含量为５５－７０％。

【技术特征摘要】

【专利技术属性】
技术研发人员：林家生，文迪田，黄校良，贾平，刘建辉，黄金宝，周玉球，汪海应，杨文华，
申请(专利权)人：广东博华陶瓷有限公司，
类型：发明
国别省市：44[中国|广东]