本发明专利技术具体涉及一种耐火自流浇注料的制备方法。本发明专利技术所采用的技术方案是：将３５～５５ｗｔ％的矾土颗粒、５～２０ｗｔ％的矾土细粉、５～２５ｗｔ％的刚玉细粉、５～３０ｗｔ％的电熔陶粒砂、２～１０ｗｔ％的纯铝酸钙水泥、２～６ｗｔ％的硅微粉、２～１０ｗｔ％的α－Ａｌ↓［２］Ｏ↓［３］微粉、０．１～０．２ｗｔ％的减水剂混合，搅拌均匀制得。本发明专利技术所制备的耐火自流浇注料具有不偏析、流动性好、易施工、致密度高、强度好、成本较低的特点。广泛适用于加热炉炉衬、钢包永久层、中间包永久层等热工窑炉。

Refractory gravity pouring material and preparation method thereof

The invention relates to a preparation method of refractory gravity pouring material. The technical proposal of the invention is: 35 ~ 55wt% ~ 5 alumina particles, alumina powder, 5 ~ 20wt% corundum powder, 5 ~ 25wt% 30wt% fused ceramite, 2 ~ 10wt% of pure calcium aluminate cement, silica powder, 2 ~ 6wt% 2 ~ 10wt% alpha Al: 2 O: 3 micro powder, 0.1 ~ 0.2wt% water reducing agent mixing, stirring evenly to make. The refractory gravity pouring material prepared by the present invention has the characteristics of non segregation, good fluidity, easy construction, high density, good strength and low cost. Widely used in heating furnace lining, ladle permanent layer, tundish, permanent layer and other thermal furnace.

【技术实现步骤摘要】

【技术保护点】
一种耐火自流浇注料的制备方法，其特征在于将３５～５５ｗｔ％的矾土颗粒、５～２０ｗｔ％的矾土细粉、５～２５ｗｔ％的刚玉细粉、５～３０ｗｔ％的电熔陶粒砂、２～１０ｗｔ％的纯铝酸钙水泥、２～６ｗｔ％的硅微粉、２～１０ｗｔ％的α－Ａｌ↓［２］Ｏ↓［３］微粉、０．１～０．２ｗｔ％的减水剂混合，搅拌均匀制得。

【技术特征摘要】

【专利技术属性】
技术研发人员：李远兵，覃显鹏，李亚伟，赵雷，雷中兴，金胜利，李淑静，
申请(专利权)人：武汉科技大学，
类型：发明