本发明专利技术涉及用于制备灌浆料的组合物及其制备方法。一种用于制备灌浆料的组合物，所述的组合物包括下列各组分：水泥１００；水４５－５０；掺和料３１－３５；减水剂１．２－１．５；黄沙１４０－１５０；钢纤维２０－２１；碎石２６５－２７５；所述各组分含量均为重量份。所述的制备方法按下述步骤操作：步骤一，开启强制式搅拌机，空转２～３分钟，确认设备无故障；步骤二，按照上述组分配比，投入碎石，黄沙和钢纤维，搅拌６０ｓ；步骤三，加入水泥，搅拌３０秒；步骤四，加入减水剂，搅拌１８０ｓ以上；步骤五，出料，每２５ｋｇ装袋。

Composition for preparing grouting material and preparation method thereof

The invention relates to a composition for preparing grouting material and a preparation method thereof. A composition for preparing grouting material, the composition comprises the following components: 100 water cement; 45 - 50; 31 - 35 admixture superplasticizer; 1.2 - 1.5; 140 - 150 sand steel fiber; 20 - 21; 265 - 275 of the gravel; content of each component was weight. The preparation method comprises the following steps: Step 1, open operation forced mixer, idling 2 ~ 3 minutes, confirmed that no fault; step two, according to the investment ratio, gravel, sand and steel fiber, mixing 60s; step three, adding cement, stirring for 30 seconds; step four, adding water reducing agent, mixing 180s above; step five, discharge, per 25kg bag.

【技术实现步骤摘要】

本专利技术涉及用于制备灌漿料的组合物及其制备方法。
技术介绍
灌浆料属于干粉砂浆的一种，由于其具有高流动性，强度高的特点，在 工程施工中越来越多的被使用。但是现有的灌浆料在使用当中，人们发现其 收縮率大，多空隙、质地疏松、耐动荷载性差。这些弊病往往会导致釆用此 灌浆料的工程质量低下， 一旦发生事故，往往造成人员伤亡，引起恶劣的社会影响。
技术实现思路
本专利技术旨在解决现有灌浆料的上述缺陷，提供一种用于制备灌浆料的组 合物及其制备方法。本专利技术与传统的灌浆料相比，具有收縮小、密实性好、 孔隙少和耐动荷载性好等特点。本专利技术是这样实现的 一种用于制备灌浆料的组合物，所述的组合物包 括下列各组分(对于重量份为100的水泥的所述各组分重量份) 水泥 100 水 45-50掺和料31-35 减水剂 1.2-1.5黄沙 140-150 钢纤维 20-21碎石 265-275。所述组合物的一个典型配比为(对于重量份为100的水泥的所述各组分 重量份)水泥 100 水 47掺和料33 减水剂 1.3黄沙 145 钢纤维 20.7碎石 270。所述水泥强度大于42.5MPa;所述本文档来自技高网...

【技术保护点】
一种用于制备灌浆料的组合物，其特征在于，所述的组合物包括下列各组分：水泥１００水４５－５０掺和料３１－３５减水剂１．２－１．５黄沙１４０－１５０钢纤维２０－２１碎石２６ ５－２７５所述各组分含量均为重量份。