本发明专利技术涉及一种曝气生物滤池填料及其制备方法，由３０－４０％污泥、１７－３２％炼铁炉渣、１８％－２０％粘土、１８％－２０％页岩为原料，在１１００－１１８０℃下焙烧１５－３０分钟制成。本发明专利技术大量使用污水处理厂污泥，粘土使用比例低，既解决了污泥的处理问题，使污泥资源化，又节约粘土资源，有利于环境保护。本发明专利技术的总磷（ＴＰ）平均去除率比德国火山灰填料高２０％，化学需氧量（ＣＯＤ）和氨氮（ＮＨ↓［３］－Ｎ）去除效果与德国火山灰填料基本相同。

Biological aerated filter filler with waste material as main raw material and preparation method thereof

The invention relates to a biological aerated filler and its preparation method, from 30 - 40%, 17 - 32% sludge iron smelting slag, 18% - 20%, 18% - 20% clay shale as raw material, in the 1100 - 1180 C 15 - 30 minutes into the roasting. The invention uses sludge from sewage treatment plants in large amount, and has low utilization ratio of clay. The utility model not only solves the problem of sludge treatment, makes the sludge resource, but also saves the clay resources, and is favorable for environmental protection. The invention of the total phosphorus (TP) removal rate is 20% higher than the German volcano ash filling, chemical oxygen demand (COD) and ammonia (NH: 3 N) removal and Germany volcano ash filling is basically the same.

【技术实现步骤摘要】

本专利技术属于环境应用材料领域和污水处理
，涉及一种曝气生物滤池填料及其 制备方法。
技术介绍
曝气生物滤池是将生物接触氧化法与给水过滤相结合的一种好氧生物膜法废水处理 工艺，属于生物过滤技术，它主要是利用填料的拦截和填料上生物膜的生物降解双重作用 将污染物加以去除。理想的生物滤池填料一般应当具备较大比表面积、粗糙的表面、适当密度等良好物理 性能，以及生物亲和性和较强的稳定性。目前，德国的火山灰填料以其密度小、硬度大、 生物附着能力强、磨损率小等优点，在我国占据了较大的市场，但是其价格昂贵，并且除 磷效果不好。国产填料主要以粘土为主要原料，需要消耗大量粘土资源，不利于生态平衡 和环境保护，而且使得填料的成本较高。利用城市污水处理厂的污泥代替部分粘土烧制填料，是一种经济有效的污泥无害化和 资源化途径，污泥中含有的有机物在高温下矿化产生的C02气体可以充当造孔剂，能够增大填料的比表面积。申请号为CN200510010577.1的专利文件公开了一种以粘土、污泥和 粘结剂为原料制成的填料及其制备方法。该填料具有强度高，不易破损，滤料表面粗糙使 得微生物容易挂膜等优点，但是粘土使用比例本文档来自技高网...

【技术保护点】
一种以废料为主要原料的曝气生物滤池填料，是通过高温焙烧制成的表面粗糙的颗粒，其特征在于是由污泥、炼铁炉渣、粘土、页岩为原料，各原料的重量百分比为：污泥３０－４０％、炼铁炉渣１７－３２％、粘土１８％－２０％、页岩１３－３５％。