The invention belongs to the technical field of magnesium coating, in particular to a magnesium coating in a tundish. The technical proposal is: 89 ~ 96wt%, 1 ~ 3wt% intermediate magnesia clay, silica powder, 0.5 ~ 2.5wt% 1 ~ 3wt%, 1 ~ 5wt% fiber paper anhydrous Magnesium Sulfate hybrid mixture, plus the 12 ~ 20wt% water, and then evenly stirring for tundish magnesium coating. Of which: the grain size of medium magnesia is: 3 to 0.088mm with particle size ranging from 58 to 61wt%, and the particle size is from 0.088 to 0mm, accounting for 31 ~ 35wt%. The present invention in addition with anhydrous magnesium coating in Magnesium Sulfate coatings increased, the reduction in water consumption, condensation hardening time under normal temperature accelerated, intensity significantly increased, the flexural and compressive strength of 110 DEG C * 24h also increased significantly, and does not affect the coating high temperature performance, convenient construction, can make the enterprise the production efficiency is improved obviously.
【技术实现步骤摘要】
本专利技术属于镁质涂料
，具体涉及一种中间包镁质涂料。
技术介绍
随着新的冶炼技术和连铸新工艺的快速发展，对耐火材料的要求越来越苛刻，使连铸中 间包用涂料愈来愈受到重视，同时也面临着前所未有的挑战。中间包是钢包与结晶器之间用 于钢水过渡的装置，它不仅负责钢水从钢包到结晶器之间的分流、整流和贮存钢水的作用， 而且还具有钢水的精炼和非金属夹杂去除的新功能。在连铸生产过程中针对中间包的使用条件，中间包用镁质涂料具有以下优异性能-(1) 常温或低于50 150'C时具有良好的涂抹性能；(2) 常温下无裂缝，且经快速烘烤至使用温度(IOO(TC以上)后不爆裂；(3) 使用过程中具有良好的抗热冲击性和耐侵蚀性能；(4) 具有较低的导热系数，隔热性好；(5) 使用后的残余涂层具有良好的解体性能，易翻包；(6) 具有净化钢水功能，能进一步提高钢坯质量等。因镁质涂料具有以上诸多优点，故在最近几年中得到了迅速的发展。但是由于镁质涂料 在常温下的凝聚硬化时间较长，且强度偏低，给生产施工带来不便，不能满足高产高质量的 生产要求,在钢铁企业竞争日夜激烈的今天严重地影响了生产效率。向...
【技术保护点】
一种中间包镁质涂料，其特征在于先将８９～９６ｗｔ％的中档镁砂、１～３ｗｔ％的粘土、０．５～２．５ｗｔ％的硅微粉、１～３ｗｔ％的纸纤维、１～５ｗｔ％无水硫酸镁混合，再外加上述混合料的１２～２０ｗｔ％的水，然后搅拌均匀。
【技术特征摘要】
【专利技术属性】
技术研发人员：汪厚植，顾华志，龚志云，
申请(专利权)人：武汉科技大学，
类型：发明
国别省市：83[中国|武汉]