一种用于制造通信管道人孔的树脂混凝土制造技术

本发明专利技术公开了一种用于制造通信管道人孔的树脂混凝土，其特征在于该混凝土主要由骨料５０～８０重量份，粉料１０～２０重量份，不饱和聚酯树脂８～１２重量份，外加剂０．５～５重量份制成；其中，外加剂包括低收缩剂和硬化剂；低收缩剂为颗粒状聚苯乙烯的苯乙烯溶液或／和聚醋酸乙烯酯低收缩剂，用量为０．１～１．５重量份。该树脂混凝土通过降低不饱和聚酯树脂的用量，调整骨料和粉料的组成以及低收缩剂的使用得到高效树脂混凝土，采用此种混凝土制造的通信管道人孔具有无裂纹、高强度等良好的物理性能。

Resin concrete used for making communication pipe manhole

The invention discloses a method for manufacturing the resin concrete communication pipeline manhole, characterized in that the concrete aggregate is mainly composed of 50 to 80 parts by weight of powder, 10 to 20 parts by weight of unsaturated polyester resin, 8 to 12 parts by weight, 0.5 to 5 parts by weight of admixture which made; including low shrinkage agent and admixture hardening agent; low shrinkage agent for granular polystyrene solution of styrene or / and polyvinyl acetate low shrinkage agent dosage is 0.1 to 1.5 parts by weight. The resin concrete by reducing the amount of unsaturated polyester resin, adjusting aggregate and powder composition and low shrinkage agent using high resin concrete, the concrete made by communication pipeline manhole has physical properties with no crack, high strength and good.

【技术实现步骤摘要】

本专利技术属于混凝土
，具体涉及一种用于制造通信管道人孔的树脂混凝土。本 专利技术通过选择合适树脂含量，合适的外加剂包括低收縮剂、硬化剂等，得到具有高强度的 新型高效树脂混凝土及其由该混凝土制成的通信管道人孔。
技术介绍
树脂混凝土是以合成树脂(Polymer Resin)加上适量的固化剂、增韧剂、稀释剂及填 料作为胶粘剂，以砂、石为骨料，经混合、成型、固化而成的一种复合材料。树脂混凝土 的研发是从二十世纪五十年代开始的，尤其在美国、日本、英国、德国、前苏联等国家积 极开展对树脂混凝土的研究与开发。其中又以日本、前苏联及德国研究开发较为活跃。1955 年在日本最初研究开发的是日本电信，研究开发以不饱和树脂为粘合剂制造树脂混凝土去 改善地下通信设施。德国在1962年至1963年间发表的也是以不饱和树脂以及环氧树脂为 粘合剂的树脂混凝土制造技术。从此世界各地对树脂混凝土的关心程度越来越高，它的独 特性能和潜在用途引起了人们的重视，从1967年起有关这方面的国际会议也在频繁召开。树脂混凝土由于其具有良好的耐侵蚀、耐磨、耐水和抗冻能力及力学性能，弥补了水泥 混凝土抗拉强度低、抗拉应变本文档来自技高网...

【技术保护点】
一种用于制造通信管道人孔的树脂混凝土，其特征在于该混凝土主要由骨料５０～８０重量份，粉料１０～２０重量份，不饱和聚酯树脂８～１２重量份，外加剂０．５～５重量份制成；其中，外加剂包括低收缩剂和硬化剂；低收缩剂为颗粒状聚苯乙烯的苯乙烯溶液或／和聚醋酸乙烯酯低收缩剂，用量为０．１～１．５重量份。

【技术特征摘要】

【专利技术属性】
技术研发人员：薛平，李建新，
申请(专利权)人：江苏普利匡聚合物材料有限公司，
类型：发明
国别省市：84[中国|南京]