The invention discloses a high abrasion resistance and thermal shock resistance of high alumina brick, which comprises the following components in parts by weight: 3 ~ 5mm 5 ~ 15 grade bauxite aggregate, 1 ~ 3mm 30 ~ 40 grade bauxite aggregate, 0 ~ 1mm 10 ~ 20 grade bauxite aggregate, super fine alumina powder from 20 to 30 a zircon powder, 5 - 7, Suzhou No. 2 mud 1 - 3, 8 to 10 portions of binder and water from 4 to 6. The invention also discloses the manufacturing method of the high abrasion resistant thermal shock resistant high alumina brick. The high abrasion resistant thermal shock resistant high alumina brick has high strength, high refractoriness, high abrasion resistance and thermal shock resistance. The utility model is suitable for the circulating fluidized bed boiler, the cyclone separator flue, the cyclone separator, the straight section and the cone, the return feeder, the metallurgical industrial furnace and other thermal equipment. The manufacturing process of the invention is simple and easy to implement.
【技术实现步骤摘要】
本专利技术属耐火材料领域，尤其涉及。
技术介绍
在循环流化床锅炉上，旋风分离器是流化床锅炉最关键的部件之一，这些部位使用 的耐火材料必须具有较好的耐磨性和热震稳定性。这些部位最常使用的耐火材料为PA 砖或高铝浇注料。旋风分离器进口烟道、分离器直段和锥段，该部位流速高、灰浓度高、 磨损严重，特别是烟气进口切向120。角度范围内，由于高速气固两相流的冲刷，致使该 部位磨损非常严重。
技术实现思路
本专利技术正是为了克服上述不足，所要解决的技术问题是提供一种适用于循环流化床 锅炉的高耐磨抗热震高铝砖。本专利技术还要解决的技术问题是提供上述高耐磨抗热震高铝砖的制造方法。为解决上述技术问题，本专利技术所采用的技术方案如下-一种高耐磨抗热震高铝砖，它包括如下重量份数的组分3~5mm特级矾土骨料5 '15份l~3mm特级矶土骨料30 '40份0 lrnrn特级矶土骨料10 ~'20份特级矾土细粉20 ~30份锆英砂细粉~7份苏州2号泥1~3份复合结合剂8 IO份水4~6份。其中，所述的特级矾土细粉为220目。 其中，所述的锆英砂细粉为320目。其中，所述的复合结合剂为A1203、...
【技术保护点】
一种高耐磨抗热震高铝砖，其特征在于它包括如下重量份数的组分： ３～５ｍｍ特级矾土骨料 ５～１５份 １～３ｍｍ特级矾土骨料 ３０～４０份 ０～１ｍｍ特级矾土骨料 １０～２０份 特级矾土细粉 ２０～３０份 锆英砂细粉 ５～７份 苏州２号泥 １～３份 复合结合剂 ８～１０份 水 ４～６份。
【技术特征摘要】
【专利技术属性】
技术研发人员：毛荣新，毛荣棠，毛小平，杨华峰，
申请(专利权)人：江苏耐基炉衬有限公司，
类型：发明
国别省市：32[中国|江苏]