烧结α－β氧化铝砖制造技术

本发明专利技术涉及一种烧结α－β氧化铝砖，其配方为：５－１ｍｍ　α－β氧化铝颗粒３５－５０％、＜１ｍｍα－β氧化铝粉料１５－２５％、＜０．０８８ｍｍ　α－β氧化铝粉料１５－２０％、＜０．０４４ｍｍ　α氧化铝粉料０－１０％、＜０．０１０ｍｍ　α氧化铝粉料０－６％、纯铝酸钙水泥０－１０％、六偏磷酸钠０－０．３％。本发明专利技术工艺成熟、制作方便、成本较低，主要用于玻璃熔窑接触玻璃液部位，特别是料道等部位，与熔铸α－β氧化铝砖在玻璃熔窑配套使用，可以满足玻璃熔窑对于α－β氧化铝砖的需求。

Sintered alpha beta alumina brick

The present invention relates to a sintered alpha beta alumina brick, the formula is: 5 1mm alpha beta alumina particles of 35 - 50%, 1mm < alpha beta alumina powder is 15 - 25%, 0.088mm < alpha beta alumina powder is 15 - 20%, 0.044mm < alpha alumina powder of 0 - 10%, 0.010mm < 0 - 6% alpha alumina powder, pure calcium aluminate cement 0 - 10%, six - 0.3% 0 sodium metaphosphate. The present invention has mature technology, convenient manufacture, low cost, mainly used for glass melting furnace molten glass contact parts, especially the material and other parts, and cast the alpha beta alumina brick in glass furnace can meet the demand for supporting the use of alpha beta alumina brick for glass furnace.

【技术实现步骤摘要】

本专利技术涉及一种玻璃窑用烧结a-P氧化铝砖及其制备方法，属于耐火材料
该 种耐火材料以电熔a - e氧化铝颗粒和粉料以及a氧化铝粉料为主要原料，以纯铝酸钙水泥和 六偏磷酸钠为添加剂，根据配比将以上原料加入一定量水分混制好后加入到模具中经震动成 型，固化干燥后的坯体再经过高温烧成，冷加工后作为成品使用。本专利技术工艺成熟、制作方 便、成本较低，所制产品主要用于玻璃熔窑接触玻璃液部位，特别是料道等部位。
技术介绍
现代玻璃熔窑对于耐火材料的要求日渐苛刻，长寿命、对玻璃液低污染的耐火材料在玻 璃熔窑的用量越来越大。a-e氧化铝耐火材料具有以上优点，因此熔铸a-e氧化铝砖近年 来在玻璃熔窑的配置量不断增加。熔铸a-e氧化铝耐火材料在玻璃熔窑的使用经验证明该 种耐火材料在135(TC以下具有非常好的抗玻璃液侵蚀性能，而且对玻璃液的污染倾向低用 于火焰空间，还具有抗碱蒸气侵蚀的优点。但是采用烙铸方法生产a-P氧化铝耐火材料对于 形状简单的制品，产品质量和成品率能够保证，如果生产形状复杂的制品或者超大型制品(例 如玻璃窑大型料道)，由于縮孔和退火应力，产品的质量波动大，成品率低，很难本文档来自技高网...

【技术保护点】
一种烧结α－β氧化铝砖，其特征在于：所述砖的配方为：　５－１ｍｍα－β氧化铝颗粒　３５－５０％　＜１ｍｍα－β氧化铝粉料　１５－２５％　＜０．０８８ｍｍα－β氧化铝粉料　１５－２０％　＜０．０４４ｍｍα氧化铝粉料　０－１０％　＜０．０１０ｍｍα氧化铝粉料　０－６％　纯铝酸钙水泥　０－１０％　六偏磷酸钠　０－０．３％　所述的α－β氧化铝颗粒系以电熔工艺生产的高纯原料，Ａｌ↓［２］Ｏ↓［３］＞９３％，Ｎａ↓［２］Ｏ≤４，所述的α氧化铝粉料为Ａｌ↓［２］Ｏ↓［３］含量≥９８％的氧化铝微粉，所述的纯铝酸钙水泥以ＣＡ为主要矿物成分。

【技术特征摘要】

【专利技术属性】
技术研发人员：刘锡俊，王杰曾，叶亚红，陈龙，李鹏海，王俊涛，赵洪亮，毛利民，
申请(专利权)人：瑞泰科技股份有限公司，
类型：发明
国别省市：11[中国|北京]