The invention discloses a method with gold tailings as the main raw material for the production of glass products, ingredients with chemical composition: 2 O: Cao SiO 3: 2 three yuan in the phase diagrams of the system requirements, the process comprises the following steps: selection of raw materials, ingredients, high temperature melting, molding and demoulding, nucleation and crystallization, cooling and postprocessing. Using this method, on the one hand, we can make use of waste residue, turn waste into treasure and control the environment. On the other hand, we can produce all kinds of glass ceramics products of high strength, such as decorative plates, bearings, valves, tableware and so on.
【技术实现步骤摘要】
本专利技术涉及尾矿渣再利用领域，具体地说涉及一种。随着工矿企业的迅速发展，工业矿渣、废渣的种类和积蓄量逐年增加，占用了耕地，污染了环境，人们已朝着这个方向努力，在废渣利用、治理环境方面取得了很大进展。一专利申请文件，申请号为85100521，名称为“粉煤灰废渣微晶玻璃”的专利技术创造报道了粉煤灰的利用情况；另一专利申请文件，申请号为91106992.5，名称为“磷尾矿渣制微晶玻璃大理石的方法”的专利技术创造报道了磷尾矿渣的利用情况。近年来，淘金工业的规模越来越大，黄金尾矿的堆积已引起了人们的关注，急需人们开发研究对黄金尾矿的再次利用。本专利技术的目的是提供一种对黄金尾矿的再次利用的方法，具体地提供一种。本专利技术的目的通过以下方案来实现，依次经过如下步骤原料筛选、配料、升温至1400～1500℃保温3～6h熔化、成型、脱模，在700～800℃保温1～3h进行核化处理，再在800～9O0℃保温1～3h进行晶化处理，最后冷却，其特征在于原料配料的重量百分组成为黄金尾矿55～70工业石灰石15～36工业硼酸0～15工业氧化锌0～10工业氟化钙0～4工业硫酸钡0～1...
【技术保护点】
一种用黄金尾矿生产微晶玻璃制品的方法，依次经过如下步骤：原料筛选、配料、１４００～１５００℃保温３～６ｈ熔化、成型、脱模、在７００～８００℃保温１～３ｈ进行核化处理、再在８００～９００℃保温１～３ｈ进行晶化处理，最后冷却，其特征在于原料配料的重量百分比为：黄金尾矿５５～７０ 工业石灰石１５～３６ 工业硼酸０～１５ 工业氧化锌０～１０ 工业氧化钙０～４ 工业硫酸钡０～１４ 工业氧化铬０～５ 工业二氧化锰０～５ 工业氧化铜０～６工业氧化铁０～６ 工业无水芒硝０～５，使配料的化学组成落在ＣａＯ－Ａｌ↓［２］Ｏ↓［３］－ＳｉＯ↓［２］系统相图中，其重量百分比为Ｓｉ...
【技术特征摘要】
【专利技术属性】
技术研发人员：刘心中，李智广，李浩，纪忠广，夏候志禹，
申请(专利权)人：山东建材工业学院分院科研生产处科技开发中心，
类型：发明
国别省市：37[中国|山东]