锑钼镁低温白底釉制造技术

一种锑钼镁低温白底釉，属于搪瓷工业日用制品。本低温白底釉，由长石、硅石、氟石、硼砂、硝石、纯碱、冰晶、氧化锑、滑石、碳酸铵、钼酸铵组成。研细混均，经１１００－１１５０℃熔融、水激成瓷块，加粘土或膨润土磨成，釉浆，即涂搪制品铁坯上，干燥，经７４０－８２０℃烧成，与铁坯牢固结合，即称低温白底釉。本底釉与钛面釉及锑面釉结合，经烧成后，即为搪瓷制品。

Antimony molybdenum magnesium low temperature white glaze

The utility model relates to a low temperature white base glaze of antimony molybdenum magnesium, belonging to an enamel industrial daily product. The low temperature white glaze, composed of silica, feldspar, fluorite, borax, saltpeter, soda ash, ice, antimony oxide, talc, ammonium carbonate, ammonium molybdate. Research of fine mixing, by 1100 - 1150 DEG C melting, water shock into ceramic blocks, adding clay or bentonite into glaze, namely, enameling products iron billet, drying, by firing 740 - 820 DEG C, combined with solid iron billet, namely temperature white glaze. The base glaze is made of titanium surface glaze and antimony surface glaze, and then it is made of enamel after firing.

【技术实现步骤摘要】

本专利技术属于搪瓷工业日用制品，特别是一种锑钼镁低温白底釉。
技术介绍
搪瓷制品的瓷釉分为面釉和底釉两个部分。本技术侧重探讨底釉，底釉有黑色或蓝色，通称钴镍底釉。自1973年以后，发展应用以氧化锑和钼酸铵为密着剂，硅酸镁为光亮剂组成，即为锑钼镁低温白底釉。
技术实现思路
本专利技术的目的在于节药能源，降低瓷釉烧成温度，减少燃料消耗，延长炉窑寿命，提高产品质量、降低成本等综合效益。本专利技术的锑钼镁低温白底釉的组成1.化学成分(％)Sio243.20、Ae2O35.52、Na2O17.40、B2O39.30、CaF210.80、Na2SiF65.00、Sb2O32.10、(NH4)2CO31.4、MgSiO31.20、(HH4)2MoO41.80，合计97.72，膨胀系数319.23×10-7。2.原料配合量长石27.90、硅石25.00、氟石11.80、硼砂24.10、硝石10.00、纯碱6.80、冰晶5.00、氧化锑2.10、滑石1.20、碳酸铵1.40、钼酸铵1.80，合计117.10。本专利技术的特点搪瓷制品长时间使用黑底釉由高温880-920℃烧成温度，发展到应用白底釉，烧成本文档来自技高网...

【技术保护点】
一种锑钼镁低温白底釉，其特征是，钼酸铵、滑石、氧化锑新原料组成。

【技术特征摘要】

【专利技术属性】
技术研发人员：孙立朝，孙铭辰，孙瑛莲，孙继承，王红，王勇，方桂兰，
申请(专利权)人：孙立朝，孙铭辰，
类型：发明
国别省市：82[中国|长春]