The invention relates to an optical glass for precise pressing. The utility model belongs to the technical field of optical glass. The main is to provide a free PbO, As: 2 O: 3, refractive index (n: D) in 1.54 ~ 1.66, Abbe number (V: D) in 57 - optical glass for precision pressure within 68. It is characterized in that: according to the weight percentage by SiO: 2: 15 ~ 50% B, down 2 O: 3 to 40%: 10, Al: 2 O: 3: 0.5 ~ 5.5%, ZnO:2.0 ~ 8%, BaO:10 ~ 24%, CaO:0 ~ 15%, down ZrO 2 to 5%: 0, Nb: 2 O: 5 to 2%: 0, La: 2 O: 3 to 5%: 1, Li: 2 O:4.0 ~ 10%, K: 2 O:0 to 2% Sb, 2 O, down down 3: the composition of each component of 0 ~ 0.5%, each kind of glass components and 100%. With the transition temperature (Tg) of less than 535 DEG C, the proportion is 2.5 ~ 3.1g / cm = 3, suitable for precision press molding, excellent chemical stability, and suitable characteristics for large-scale production, mainly used in optical glass precision pressure type.
【技术实现步骤摘要】
本专利技术属于光学玻璃
具体涉及一种Si02—B203—Al203 — ZnO —BaO—CaO—Zr02—Li20—K20—La203—Nb20s体系、不含PbO、 As203的精 密压型用光学玻璃。
技术介绍
众所周知，过去具有折射率(nd)为1.54 1.66,阿贝数(Ud)为57~68范围的 光学常数的光学玻璃有重冕玻璃。例如，"玻璃组成数据手册"1991年(曰本 玻璃制品工业会发行)中，作为重冕玻璃记载有很多SK (重冕)型玻璃。但 是，由于这些玻璃一般转变温度(Tg)高，很多都超过60(TC，结果是成型温 度高。在精密压型中，如果玻璃的成型温度增高，则会减小模具的使用寿命， 增大压型件的成本。故希望玻璃的转变温度尽可能的降低。作为解决这些问题 的办法，已提出种种在玻璃组成体系中加大量碱金属氧化物的玻璃。例如授 权公告号为CN1038834C的中国专利技术专利说明书揭示了一种Si02—B203 — SrO —Li20体系的玻璃，其中引入Ti02成份虽然能防止玻璃的日晒作用，但是Ti02 的引入将会将玻璃的短波截止波长向波长长的方向移动，同时将加...
【技术保护点】
一种精密压型用光学玻璃，其特征是：按重量百分比计由ＳｉＯ↓［２］：１５．０～５０．０％，Ｂ↓［２］Ｏ↓［３］：１０．０～４０．０％，Ａｌ↓［２］Ｏ↓［３］：０．５～５．５％，ＺｎＯ：２．０～８．０％，ＢａＯ：１０～２４％，ＣａＯ：０～１５．０％，ＺｒＯ↓［２］：０～５．０％，Ｎｂ↓［２］Ｏ↓［５］：０～２．０％，Ｌａ↓［２］Ｏ↓［３］：１．０～５．０％，Ｌｉ↓［２］Ｏ：４．０～１０．０％，Ｋ↓［２］Ｏ：０～２．０％，Ｓｂ↓［２］Ｏ↓［３］：０～０．５％范围的各成分组成，每种玻璃的各个成分之和为１００％。
【技术特征摘要】
【专利技术属性】
技术研发人员：戎俊华，李克炎，张卫，陈艳丽，黄少林，
申请(专利权)人：湖北新华光信息材料股份有限公司，
类型：发明
国别省市：42[中国|湖北]