The present invention provides a protective film containing rubber plate, the plate is coated with a layer of protective film thickness of 0.1 0.3mm, the protective film consists of 100 water samples; 3 to 5 portions of polyvinyl alcohol; 20 to 30; 2 to 3 portions of glycerol; defoaming agent 0.01 ~ 0.02; dispersant 0.1 ~ 0.2; antiseptic 0.1 - 0.2; 0.5 - 2 color crystal. The invention can meet the various special-shaped plate, the invention can produce a new type of Na2S with protective film, no matter what is the shape of rubber plate surface, can be coated, coated with rubber plate to achieve the perfect effect, the concave convex structure can be multi brushing several times, in order to make the film after drying the coating effect is better.
【技术实现步骤摘要】
本专利技术涉及一种橡胶保护膜技术应用和新型高分子功能材料的应用技术。
技术介绍
船舶制品生产过程中，为了达到减震降噪的效果，要大量使用橡胶板材，而橡胶板材表面柔软，与其它产品部件组装连接时，不可避免的会有刮、涂、撞击、磨损等外部伤害，导致其表面因反复摩擦受到破坏，并粘上难以清除的污渍，导致后期清洁工程量巨大。现在常用的保护膜一般是PE材质的保护膜，PE保护膜中又以黑白膜和蓝色保护膜的使用频率最高。但是，市场上的PE保护膜一般都是用于平板，对于表面因特殊需要有凹凸不平的地方，如门把手处，PE膜并不能起到保护作用。
技术实现思路
本专利技术的专利技术目的是为了克服上述问题，设计了能对橡胶板表面进行保护，防止磨损、粘上污渍，又能在使用的时候较容易的一种橡胶保护膜。本专利技术的技术方案是：一种含保护膜的橡胶板，其特征在于，其板面上涂有一层厚度0.1-0.3mm的保护膜，所述保护膜的组份为：水100份聚乙烯醇3～5份乙醇20～30份甘油2～3份消泡剂0.01～0.02份分散剂0.1～0.2份防腐剂0.1～0.2份色晶0.5～2份。进一步地，上述的消泡剂磷酸三丁酯。进一步地，上述的分散剂为不饱和多元羧酯聚合物与有机硅氧烷共聚物的混合物。进一步地，上述的防腐剂苯酚。本专利技术可满足各种异型板材的使用，本专利技术生产一种可以现配现用的新型保护膜，无论橡胶板表面是什么形状，都可以经过涂抹，达到完美包覆橡胶板的效果，对于凹凸结构处可以多涂刷几遍，以使风干后的薄膜包覆效果更好。附图说明图1是本专利技术的橡胶板的结构示意图；附图标记：1-保护膜；2-橡胶板。具体实施方式下面结合附图...
【技术保护点】
一种含保护膜的橡胶板，其特征在于，其板面上涂有一层厚度0.1‑0.3mm的保护膜，所述保护膜的组份为：水 100份聚乙烯醇 3～5份乙醇 20～30份甘油 2～3份消泡剂 0.01～0.02份分散剂 0.1～0.2份防腐剂 0.1～0.2份色晶 0.5～2份。
【技术特征摘要】
1.一种含保护膜的橡胶板，其特征在于，其板面上涂有一层厚度0.1-0.3mm的保护膜，所述保护膜的组份为：水100份聚乙烯醇3～5份乙醇20～30份甘油2～3份消泡剂0.01～0.02份分散剂0.1～0.2份防腐剂0.1～0...
【专利技术属性】
技术研发人员：谢文奇，程久益，鲁程，
申请(专利权)人：咸宁海威复合材料制品有限公司，
类型：发明
国别省市：湖北;42