The present invention relates to the field of concrete production, in particular to a concrete grinding agent; its quality parts are as follows: high calcium sulfur aluminum clinker 10 18 copies, three monoisopropanolamine 10 15 copies, 5 copies, 3 anhydrite 2 magnetite 8, carboxymethyl cellulose 5, 3 zeolitization 10 perlite powder 30, 2 Nano Silica 6, six sodium hexametaphosphate 2.4 5.6 copies, 6 copies, 2 TiO2 water cellulose 1.8 4.8, water 50 60; do not change in mill conditions, can increase the mill output rate of 10 30%, and at the same time effectively reduce grinding phenomenon, concrete particle gradation optimization; can improve the dispersibility of the material in the mill, effectively eliminate concrete fine particles by electrostatic adsorption and ball grinding paste bag phenomenon.
【技术实现步骤摘要】
本专利技术涉及混凝土生产领域，尤其是一种混凝土助磨剂。
技术介绍
混凝土助磨剂是一种改善水泥粉磨效果和性能的化学添加剂，可以显著提高混凝土产量、各龄期混凝土强度，改善其流动性。混凝土助磨剂能大幅度降低粉磨过程中形成的静电吸附包球现象，并可以降低粉磨过程中形成的超细颗粒的再次聚结趋势。混凝土助磨剂也能显著改善混凝土流动性，提高磨机的研磨效果和选粉机的选粉效率，从而降低粉磨能耗。使用助磨剂生产的混凝土具有较低的压实聚结趋势，从而有利于混凝土的装卸，并可减少混凝土的挂壁现象。作为一种化学添加剂，助磨剂能改善混凝土颗粒分布并激发水化动力，从而提高混凝土早期强度和后期强度。国内大多采用工业纯聚合有机盐和无机盐为助磨剂的主要成分，成本较高，技术经济指标不适应实际生产情况，产品适应面较窄，特别对于温度较高的物料还没有合适的产品。即使对于不同生产厂家的同种产品应用于不同厂家，也存在效果差异较大的情况。现有产品无法充分发挥该产品改善粉磨物料粘附效果，且未能将多种有效助磨成分配合在一起，从而发挥最佳粉磨效果。
技术实现思路
本专利技术要解决的技术问题是：克服现有技术中的不足，提供一种保水性好、能改善水泥比表面积和外观的混凝土助磨剂。为解决上述技术问题，本专利技术采用的技术方案如下：一种混凝土助磨剂，其质量份组成如下：高钙硫铝熟料10-18份、三异丙醇胺10-15份、硬石膏3-5份、四氧化三铁2-8份、羧甲基纤维素3-5份、沸石化珍珠岩粉10-30份、纳米二氧化硅2-6份、六偏磷酸钠2.4-5.6份、二氧化钛2-6份、保水纤维素1.8-4.8份、水50-60份。作为优选，所述的一...
【技术保护点】
一种混凝土助磨剂，其特征在于其质量份组成如下：高钙硫铝熟料10‑18份、三异丙醇胺10‑15份、硬石膏3‑5份、四氧化三铁2‑8份、羧甲基纤维素3‑5份、沸石化珍珠岩粉10‑30份、纳米二氧化硅2‑6份、六偏磷酸钠2.4‑5.6份、二氧化钛2‑6份、保水纤维素1.8‑4.8份、水50‑60份。
【技术特征摘要】
1.一种混凝土助磨剂，其特征在于其质量份组成如下：高钙硫铝熟料10-18份、三异丙醇胺10-15份、硬石膏3-5份、四氧化三铁2-8份、羧甲基纤维素3-5份、沸石化珍珠岩粉10-30份、纳米二氧化硅2-6份、六偏磷酸钠2.4-5.6份、二氧化钛2-6份、保水纤维素1.8-4.8份、水50-60份。2.根据权利要求1所述的一种混凝土助磨剂，其特征在于：所述保水纤维素的制备方法如下：（1）配置四氧化三铁溶液，所述四氧化三铁溶液的摩尔比为1:1.1-1.4；（2）加入水、三异丙醇胺加热至130-140℃，滴加四氧化三铁溶液，三异丙醇胺与四氧化三铁...