一种废旧橡胶改性沥青再生的生产工艺制造技术
Process for regenerating waste rubber modified asphalt
The invention discloses a production process of waste rubber modified asphalt, comprising the following steps: the asphalt melting rapid heating input after the colloid mill in a colloid mill, rubber powder and additives shearing swelling, swelling again after the input of colloid mill grinding, so repeated 3 to 6 times after the development of modified asphalt products. The modified asphalt is added to a certain proportion to melt the new material and the old material, and then the asphalt product is recycled. The process is simple, the modified asphalt recycling, the use of waste rubber powder instead of asphalt modifier, reduce costs and enhance the performance and durability of the pavement, to extend the pavement performance.
【技术实现步骤摘要】
本专利技术属于建筑材料
，特别是涉及一种废旧橡胶改性沥青再生的生产工艺。
技术介绍
我国是世界上最大橡胶销售国，每年废旧橡胶超过100万吨。橡胶具有抗热性、抗降解以及抗机械性能，橡胶生产数量逐渐加大，不仅产生巨大的橡胶资源浪费，同时还有可能引发火灾、传播疾病，给生态环境与人类健康带来较大的危害。将废橡胶应用于改性沥青，改善路面使用性能的同时，还可以充分发挥再生资源，在保护环境方面发挥重要的作用。沥青路面通常用于铺筑路面的面层，受车辆荷载作用和大气因素的影响，长期使用的沥青路面老化后会出现开裂、坑槽、车辙印等，影响过往车辆行驶。以往维护路面的方法一般都将旧沥青混合料清除掉，然后重新铺筑。通过这种方法能够保证沥青路面性能完好，但同时也产生了大量的沥青混合料废弃物。再生沥青是将旧沥青路面翻挖，将其回收、破碎、筛分后，与再生剂、新沥青材料、新集料等按一定比例重新拌和混合料，使之能够满足一定的路用性能并用其重新铺筑路面的工艺技术。再生沥青不但节约材料降低路面造价，也使得资源得到再利用，减少了废旧物对环境的污染，具有明显经济效益和社会效益。目前，沥青混凝土再生技术的工...
【技术保护点】
一种废旧橡胶改性沥青再生的生产工艺，其特征在于，包括以下步骤：步骤1：将基质沥青加热至熔融；步骤2：熔融的基质沥青通过换热器快速升温至180～200℃后输入胶体磨；步骤3：将橡胶粉和助剂按一定比例输送至所述胶体磨中形成混合物，将混合物高速剪切研磨100‑120分钟，形成沥青混合料；步骤4：将沥青混合料输入溶胀罐中进行溶胀，溶胀后的沥青混合料再次输入胶体磨中研磨，研磨后输入溶胀罐中溶胀，如此反复3～6遍得改性沥青半成品；步骤5：将改性沥青半成品泵入带有搅拌器的储存罐，发育1～2小时，得改性沥青成品；步骤6：将新料加热至190～220℃，旧料加热至100～120℃，按一定配比分...
【技术特征摘要】
1.一种废旧橡胶改性沥青再生的生产工艺，其特征在于，包括以下步骤：步骤1：将基质沥青加热至熔融；步骤2：熔融的基质沥青通过换热器快速升温至180～200℃后输入胶体磨；步骤3：将橡胶粉和助剂按一定比例输送至所述胶体磨中形成混合物，将混合物高速剪切研磨100-120分钟，形成沥青混合料；步骤4：将沥青混合料输入溶胀罐中进行溶胀，溶胀后的沥青混合料再次输入胶体磨中研磨，研磨后输入溶胀罐中溶胀，如此反复3～6遍得改性沥青半成品；步骤5：将改性沥青半成品泵入带有搅拌器的储存罐，发育1～2小时，得...
【专利技术属性】
技术研发人员：张楠楠，刘永伟，彭仕军，袁强，刘华，
申请(专利权)人：四川知行路桥集团有限公司，
类型：发明
国别省市：四川;51