The invention discloses a tin zinc copper polishing agent, to the quality of a meter, comprises the following raw materials: two benzene imine 6 methylamine 15, glyceryl oleate 16 30 copies, 15 copies of polyethylene glycol 10 and sodium silicate 5 9 copies, 90 copies of 70 deionized water. Using the method of copper tin zinc polishing agent is described as follows: 1) the adjacent benzene two methylamine imines, glyceride of oleic acid and polyethylene glycol, sodium silicate in the deionized water, the temperature is 40 55 DEG C, stirring evenly; 2) the copper tin zinc surface of sandpaper and sandblasting; 3) step 1) polishing agent for tin zinc copper processing parts into the cooling to 40 55 DEG C, in the time of 30 50min; 4) the tinned copper zinc removal, cooling immediately after cleaning.
【技术实现步骤摘要】
本专利技术涉及金属表面处理
,具体涉及镀锡锌铜材抛光剂及其使用方法。
技术介绍
金属表面抛光因能降低金属制品表面粗糙度,具有增加金属制品光泽度和消除锈迹等优点,但现有用于镀锡锌铜材件的抛光剂产品存在抗腐蚀性能差,稳定性差等问题。
技术实现思路
本专利技术的目的是为了解决现有技术的不足,提供一种镀锡锌铜材抛光剂及其使用方法,制得的抛光剂尤其适用于镀锡锌铜材,抗抗腐蚀性能强,稳定性好。本专利技术采用如下技术方案:一种镀锡锌铜材抛光剂,以质量份计,包括如下原料:邻苯二甲胺亚胺6-15份、油酸甘油酯16-30份、聚乙二醇10-15份、硅酸钠5-9份、去离子水70-90份。所述的镀锡锌铜材抛光剂的使用方法为:1)将邻苯二甲胺亚胺、油酸甘油酯、聚乙二醇、硅酸钠依次加入去离子水中,温度为40-55℃,搅拌均匀;2)将待处理的镀锡锌铜材件表面进行砂纸磨平和喷砂处理;3)将步骤1)处理的镀锡锌铜材件放入冷却至40-55℃的抛光剂中,放入时间为30-50min;4)将镀锡锌铜材件取出,降温清洗后即可。本专利技术的有益效果为:本专利技术抛光剂不仅能够有效的去除镀锡锌铜材表面的油污和锈斑,使其表面光泽明亮,而且本专利技术各组分能够有效配合提高镀锡锌铜材件的抗腐蚀性能。具体实施方式下面结合实施例对本专利技术作进一步的详细描述。实施例1一种镀锡锌铜材抛光剂,以质量份计,包括如下原料:邻苯二甲胺亚胺11份、油酸甘油酯18份、聚乙二醇14份、硅酸钠8份、去离子水75份。所述的镀锡锌铜材抛光剂的使用方法为:1)将邻苯二甲胺亚胺、油酸甘油酯、聚乙二醇、硅酸钠依次加入去离子水中,温度为40 ...
【技术保护点】
一种镀锡锌铜材抛光剂,其特征在于,以质量份计,包括如下原料:邻苯二甲胺亚胺6‑15份、油酸甘油酯16‑30份、聚乙二醇10‑15份、硅酸钠5‑9份、去离子水70‑90份。
【技术特征摘要】
1.一种镀锡锌铜材抛光剂,其特征在于,以质量份计,包括如下原料:邻苯二甲胺亚胺6-15份、油酸甘油酯16-30份、聚乙二醇10-15份、硅酸钠5-9份、去离子水70-90份。2.根据权利要求1所述的镀锡锌铜材抛光剂的使用方法,其特征在于:1)将邻苯二甲胺亚胺、油...