A composite foamed cement insulation board, which consists of the following parts by weight of raw materials: 3 slag gypsum 2.3 5 copies, 4.6 copies, 7 copies of 4 fly ash, calcium stearate 1 4 copies, 5 copies of 3 perlite, 0.2 sodium metasilicate 0.6, lithium based curing agent 2 in 6, Magnesium Oxide 10 16 copies, 0.9 copies of 1.8 superplasticizer, polymer emulsion 7 chromium slag 6 14 copies, 12 copies, 13 copies of coal 7, 2 silicon waste 4 copies, 0.7 copies of the 0.4 mica, foam stabilizing agent 0.5 0.7 copies, 0.7 copies of 0.4 hydrochloride. The invention has the advantages that the composite foamed cement insulation board has the advantages of innocuity, environmental protection, low carbon, high compressive strength and bonding property and long service life.
【技术实现步骤摘要】
本专利技术涉及一种复合发泡水泥保温板。
技术介绍
水泥发泡保温板是指使用发泡水泥技术制造的保温板，水泥发泡保温板，又称发泡混凝土保温板、无机防火水泥发泡保温板保温板。是以普通硅酸盐水泥、粉煤灰、发泡剂、外加剂等为材料，经复合、搅拌、发泡、切割等工艺制成的轻质气泡状绝热材料，其突出特征是在混凝土内部形成。发泡水泥保温板是目前墙体保温和墙体保温防火隔离带最理想的保温材料，其优点是：导热系数低，保温效果好，不燃烧，防水，与墙体粘结力强，强度高，无毒害放射物质，环保。由于性能优越，越来越受到人们的欢迎。
技术实现思路
针对现有技术的不足，本专利技术要解决的问题是，提供一种复合发泡水泥保温板，无毒、环保、低碳，同时具有很好的抗压强度和粘结性，使用寿命长。为解决现有技术问题，本专利技术提供的技术方案是，一种复合发泡水泥保温板，其由以下重量份数的原料制成：炉渣3-5份，石膏2.3-4.6份，粉煤灰4-7份，硬脂酸钙1-4份，膨胀珍珠岩3-5份，偏硅酸钠0.2-0.6份，锂基固化剂2-6份，氧化镁10-16份，减水剂0.9-1.8份，聚合物乳液7-14份，铬盐渣6-12份，煤7-1...
【技术保护点】
一种复合发泡水泥保温板，其特征在于：其由以下重量份数的原料制成：炉渣3‑5份，石膏2.3‑4.6份，粉煤灰4‑7份，硬脂酸钙1‑4份，膨胀珍珠岩3‑5份，偏硅酸钠0.2‑0.6份，锂基固化剂2‑6份，氧化镁10‑16份，减水剂0.9‑1.8份，聚合物乳液7‑14份，铬盐渣6‑12份，煤7‑13份，硅废石2‑4份，云母0.4‑0.7份，稳泡剂0.5‑0.7份，盐酸0.4‑0.7份。
【技术特征摘要】
1.一种复合发泡水泥保温板，其特征在于：其由以下重量份数的原料制成：炉渣3-5份，石膏2.3-4.6份，粉煤灰4-7份，硬脂酸钙1-4份，膨胀珍珠岩3-5份，偏硅酸钠0.2-0.6份，锂基固化...
【专利技术属性】
技术研发人员：王志见，
申请(专利权)人：青岛特澳能源检测有限公司，
类型：发明
国别省市：山东;37