The invention discloses a chemical tackifying method for recycling polyethylene terephthalate, which includes ingredients: mixing the aggregate of polyethylene terephthalate and bottle flakes of polyethylene terephthalate, feeding them into a twin-screw extruder for melting extrusion, adding chain extender to react during melting extrusion, and the reaction time is 30 seconds to 5 minutes; and the diameter of the screw of the twin-screw extruder is 30 seconds to 5 minutes. The screw extruder is vacuum-pumped at a temperature of 270 C and 36-53mm. The method is simple and can effectively improve the intrinsic viscosity of recycled polyethylene terephthalate and raise the intrinsic viscosity of recycled polyethylene terephthalate to more than 0.85dl/g.
【技术实现步骤摘要】
一种回用聚对苯二甲酸乙二醇酯的化学增粘方法
本专利技术涉及一种回用聚对苯二甲酸乙二醇酯的增粘方法。
技术介绍
现有的聚对苯二甲酸乙二醇酯的回用料,由于特性粘度低,一般在0.55dl/g左右,难以制成高强度的单丝。
技术实现思路
本专利技术的目的在于提供一种能有效提高回用聚对苯二甲酸乙二醇酯特性粘度的回用聚对苯二甲酸乙二醇酯的化学增粘方法。本专利技术的技术解决方案是:一种回用聚对苯二甲酸乙二醇酯的化学增粘方法,其特征是:包括下列步骤:(1)配料:将下列质量百分比的原料混合:聚对苯二甲酸乙二醇酯的团聚料30~50%聚对苯二甲酸乙二醇酯的瓶片50~70%;(2)将上述原料送入双螺杆挤出机熔融挤出,熔融挤出过程中加入扩链剂进行反应,反应时间30秒~5分钟;双螺杆挤出机的螺杆直径为36~53mm,螺杆温度为270℃,螺杆挤出机进行抽真空处理。所述扩链剂为:二恶唑啉(BOZ)、均苯四甲酸二酐(PMDA)、二异氰酸酯的一种或者三种复配(复配比例为二恶唑啉:均苯四甲酸二酐:二异氰酸酯=20~30:30~40:30~50);扩链剂的用量为步骤(1)原料用量的0.1~0.5%。本专利技术方法简便,可有效提高回用聚对苯二甲酸乙二醇酯特性粘度,将回用聚对苯二甲酸乙二醇酯特性粘度提高到0.85dl/g以上。下面结合实施例对本专利技术作进一步说明。实施例1:一种回用聚对苯二甲酸乙二醇酯的化学增粘方法,包括下列步骤:(1)配料:将下列质量百分比的原料混合:聚对苯二甲酸乙二醇酯的团聚料40%聚对苯二甲酸乙二醇酯的瓶片60%;(2)将上述原料送入双螺杆挤出机熔融挤出,熔融挤出过程中加入扩链剂进 ...
【技术保护点】
1.一种回用聚对苯二甲酸乙二醇酯的化学增粘方法,其特征是:包括下列步骤:(1)配料:将下列质量百分比的原料混合:聚对苯二甲酸乙二醇酯的团聚料 30~50%聚对苯二甲酸乙二醇酯的瓶片 50~70%;(2)将上述原料送入双螺杆挤出机熔融挤出,熔融挤出过程中加入扩链剂进行反应,反应时间30秒~5分钟;双螺杆挤出机的螺杆直径为36~53mm,螺杆温度为270℃,螺杆挤出机进行抽真空处理。
【技术特征摘要】
1.一种回用聚对苯二甲酸乙二醇酯的化学增粘方法,其特征是:包括下列步骤:(1)配料:将下列质量百分比的原料混合:聚对苯二甲酸乙二醇酯的团聚料30~50%聚对苯二甲酸乙二醇酯的瓶片50~70%;(2)将上述原料送入双螺杆挤出机熔融挤出,熔融挤出过程中加入扩链剂进行反应,反应时间30秒~5分钟;双螺杆挤出机的螺杆直径为36~53mm...
【专利技术属性】
技术研发人员:马海燕,
申请(专利权)人:南通新帝克单丝科技股份有限公司,
类型:发明
国别省市:江苏,32