The invention discloses a preparation method of boron doped graphene / polypyrrole composite aerogels with compression recovery, which completes the reaction between pyrrole and graphene oxide and the addition of boron to graphene by hydrothermal reaction, and produces boron doped graphene / polypyrrole composite aerogels with compression recovery. It has the advantages of simple preparation method, mild reaction conditions, mass production and flexible control of composite aerogel content. The composite aerogel has good compression recovery property and can be used in compressible supercapacitors and other fields.
【技术实现步骤摘要】
具有压缩回复性的硼掺杂石墨烯/聚吡咯复合气凝胶的制备方法
本专利技术涉及气凝胶材料
,具体涉及一种具有压缩回复性的硼掺杂石墨烯/聚吡咯复合气凝胶的制备方法。
技术介绍
超级电容器也称为电化学电容器、超大容量电容器或双电层电容器,是一种优于传统电容器和普通电池的新型储能器件,具有大容量储存和快速充放电性能。目前超级电容器在电力、军品、铁路、航空航天、绿色能源等诸多领域有着巨大潜力。聚吡咯作为最常见的导电高分子,由于其制备工艺简单,环境友好,生物相容性好,导电性好,比电容高等特点而被广泛研究,但其机械性能较差、稳定性不好,这些不足限制了聚吡咯在超级电容器中的应用。石墨烯材料具有优良的电子传导能力和机械性能,易于形成三维网络结构,是制备超级电容器的理想材料之一。然而纯石墨烯材料只有双电层电容,并且石墨烯容易团聚,这也限制了其在超级电容器领域中的应用。目前的研究主要集中在将石墨烯与聚吡咯通过不同的方法进行复合,得到石墨烯/聚吡咯复合气凝胶,如中国专利CN106009444A、CN103601913A等。然而这些石墨烯/聚吡咯复合气凝胶不具有压缩回复性能,不利于将其构造可压缩超级电容器。中国专利CN106829929A公开了一种三维氮硼共掺杂的石墨烯气凝胶及其制备方法,但是该气凝胶同样不具有压缩回复性能,因而也不能用于构造可压缩超级电容器。
技术实现思路
本专利技术的目的在于克服现有技术存在的上述问题,提供一种具有压缩回复性的硼掺杂石墨烯/聚吡咯复合气凝胶的制备方法。该方法以氧化石墨烯、吡咯、四硼酸钠为原料,利用水热过程将吡咯与氧化石墨烯之间的反应以及硼对石墨烯的 ...
【技术保护点】
1.一种具有压缩回复性的硼掺杂石墨烯/聚吡咯复合气凝胶的制备方法,其特征在于,包括以下步骤:在溶液中,氧化石墨烯、四硼酸钠、吡咯经水热反应得到复合水凝胶,所得复合水凝胶经透析、冷冻、干燥即为具有压缩回复性的硼掺杂石墨烯/聚吡咯复合气凝胶。
【技术特征摘要】
1.一种具有压缩回复性的硼掺杂石墨烯/聚吡咯复合气凝胶的制备方法,其特征在于,包括以下步骤:在溶液中,氧化石墨烯、四硼酸钠、吡咯经水热反应得到复合水凝胶,所得复合水凝胶经透析、冷冻、干燥即为具有压缩回复性的硼掺杂石墨烯/聚吡咯复合气凝胶。2.根据权利要求1所述的制备方法,其特征在于:水热反应温度为80-200℃,水热反应时间为8-24h。3.根据权利要求1所述的制备方法,其特征在于:透析时间为4-48h,透析液选自体积比为1:5-400的乙醇水溶液。4.根据权利要求1所述的制备方法,其特征在于:冷冻温度为-5至-20℃,冷冻时...
【专利技术属性】