The purpose of the present invention is to provide a coating material for a laser film pressure information layer, which is composed of 20% butanone, 40% ethyl ester, 26% amido resin, 6.3% acrylic resin, 3% rosin resin and residual additives according to the weight percentage content. The quality of the laser molded product of the laser coating pressure information layer provided by the invention has also been significantly improved. The temperature resistance of the original information layer is 80 C to 100 C, and now it can reach over 130 degrees centigrade; the original coating is 8 grams per square meter, now only 6 grams; the coating speed is increased from 80 meters to 100 meters per cent; the brightness of information layer is also improved by 15%. After the new products were put into the market, they were well received by users.
【技术实现步骤摘要】
一种激光膜压信息层的涂层材料及其制备方法
本专利技术属于激光膜领域，尤其涉及一种激光膜压信息层的涂层材料。
技术介绍
激光镭射包装膜必须在原材料的表层涂入信息层，然后进行激光模压。原来的生产工艺主要由硝化棉、氨脂树与甲苯、甲醇、丁脂按比例配制涂料，再通过物理工艺对原材料进行表面涂层。由于原来的化学溶剂有毒、易燃、易挥发，生产过程中不仅对空气造成污染，而且有安全隐患。为了解决环境污染和安全隐患，我们对激光膜压信息层的涂层处理工艺进行攻关试验。
技术实现思路
本专利技术的目的提供一种激光膜压信息层的涂层材料，所述材料按重量百分比含量计由20%丁酮，40%乙酯，26%胺基树脂，6.3%丙烯酸树脂，3%松香树脂以及余量的助剂组成。作为优选，所述的助剂选自分子量调节剂、润湿剂、流平剂或消泡剂。本专利技术的目的是提供上述所述激光膜压信息层的涂层材料的制备方法，该制备方法具体为：将20%丁酮，40%乙酯，26%胺基树脂，6.3%丙烯酸树脂，3%松香树脂以及余量的助剂进行调和。其中，分子量调节剂选自正十二烷基硫醇、叔十二烷基硫醇、3-巯基丙酸异辛酯及2,4-二苯基-4-甲基-1-戊烯中的一种；润湿剂选自聚醚改性聚二甲基硅氧烷、芳烷基改性聚甲基硅氧烷、聚酯改性聚二甲基硅氧烷及有机硅硅改性聚丙烯酸酯中的一种；流平剂选自改性聚硅氧烷、有机硅改性聚丙烯酸酯及氟改性聚丙烯酸酯中的一种；消泡剂选自聚硅氧烷、矿物油及憎水颗粒消泡剂中的一种。与现有技术相比，本专利技术提供的激光膜压信息层的涂层材料激光模压产品的质量也有了明显提升。原来信息层的耐温度为80℃～100℃，现在可达到130℃以上；...
【技术保护点】
一种激光膜压信息层的涂层材料，其特征在于：所述材料按重量百分比含量计由20%丁酮，40%乙酯，26%胺基树脂，6.3% 丙烯酸树脂，3% 松香树脂以及余量的助剂组成。
【技术特征摘要】
1.一种激光膜压信息层的涂层材料，其特征在于：所述材料按重量百分比含量计由20%丁酮，40%乙酯，26%胺基树脂，6.3%丙烯酸树脂，3%松香树脂以及余量的助剂组成。2.根据权利要求1所述的激光膜压信息层的涂层材料，其特征在于：所述助...
【专利技术属性】
技术研发人员：林晓，林章薄，董德启，
申请(专利权)人：浙江宇狮包装材料有限公司，
类型：发明
国别省市：浙江,33