一种复合结构钢丝绳及其制造方法技术
A composite steel wire rope and its manufacturing method
A composite structure wire rope consists of three strand ropes. There is no independent rope core in the middle of the rope. The structure of the rope is triangular. The rope is twisted by a fiber core and inner layer steel wire and outer layer steel wire. The inner layer steel wire is not less than eight steel wires, the outer layer steel wire is not less than seven steel wire, and the outer steel wire contains one. The titanium alloy wire is located on the edge of the strands. The invention has no cordless support. When the wire rope is twisted, the wire is twisted in the center of the wire on the rope. The wire rope is twisted and the filling coefficient is large, and the technical problems of the wire rope core are easily corroded and broken, and the service life of the wire rope is improved.
【技术实现步骤摘要】
一种复合结构钢丝绳及其制造方法
本专利技术涉及一种复合结构钢丝绳及其制造方法，属于金属制品加工
技术介绍
钢丝绳通常由若干根股绳围绕一根金属绳芯构成，金属绳芯为钢芯的，绳芯容易磨损、腐蚀，钢丝绳使用寿命低，金属绳芯为纤维芯的，钢丝绳使用一定时间后，在绳芯油脂耗尽后，绳芯更容易芯易腐蚀，甚至断裂，钢丝绳外层股缺少绳芯的有效支撑，钢丝绳在使用中结构很快遭到破坏，大大降低了钢丝绳的使用寿命。
技术实现思路
本专利技术的目的是为了克服现有技术的不足，提供一种复合结构钢丝绳及其制造方法，解决了钢丝绳芯易腐蚀、断裂等技术问题，提高了钢丝绳使用寿命。本专利技术的一种复合结构钢丝绳，钢丝绳由三根股绳构成，股绳中间没有独立的绳芯，股绳结构呈三角形，所述的股绳由一根纤维芯和内层钢丝和外层钢丝捻制构成，内层钢丝不少于八根钢丝，外层钢丝不少于七根钢丝。所述的外层钢丝还包含一根钛合金丝，钛合金丝位于股绳的棱上。钢丝绳结构为3V×16、3V×18、3V×20、3V×22等。本专利技术的复合结构钢丝绳的制造方法钢丝绳捻制时，以三根股绳棱上的钛合金丝为钢丝绳的中心进行捻制。本专利技术的有益效果：本专利技术钢丝绳无绳芯支撑，钢丝绳捻制时以股绳棱上的钛丝为中心进行捻制，钢丝绳捻制结构紧密，填充系数大。钢丝绳耐腐蚀性能好，破断拉力高，解决了钢丝绳芯易腐蚀、断裂等技术问题，提高了钢丝绳使用寿命。附图说明图1为本专利技术的复合结构钢丝绳结构示意图。图中：1、外层钢丝；2、内层钢丝；3、纤维芯；11、钛合金丝。具体实施方式以下结合附图对本专利技术一种复合结构钢丝绳作进一步详细说明：本专利技术的...
【技术保护点】
一种复合结构钢丝绳，其特征是：钢丝绳由三根股绳构成，股绳中间没有独立的绳芯，股绳结构呈三角形，所述的股绳由一根纤维芯（3）和内层钢丝（2）和外层钢丝（1）捻制构成，内层钢丝（2）不少于八根钢丝，外层钢丝（1）不少于七根钢丝。
【技术特征摘要】
1.一种复合结构钢丝绳，其特征是：钢丝绳由三根股绳构成，股绳中间没有独立的绳芯，股绳结构呈三角形，所述的股绳由一根纤维芯（3）和内层钢丝（2）和外层钢丝（1）捻制构成，内层钢丝（2）不少于八根钢丝，外层钢丝（1）不少于七根钢丝。2.如权利要求1所述的复合结构钢丝绳，其特征...
【专利技术属性】
技术研发人员：严志远，黄忠渠，王小刚，贺孝宇，李伟，王发平，陆萍，
申请(专利权)人：贵州钢绳股份有限公司，
类型：发明
国别省市：贵州,52