The invention belongs to the field of iron and steel metallurgy, in particular to a production method of V, Nb, Cr micro alloy building steel bar and its LF furnace. Aiming at the problems of low nitrogen content and fewer kinds of vanadium nitride alloy used for preparing nitrogenous alloy steel, the invention provides a microalloy building steel bar containing V, Nb and Cr and its LF furnace production method. The composition of the bar: according to the weight percentage, C:0.15% ~ 0.30%, Si:0.30% ~ 1%, Mn:0.60% ~ 1.30%, N:0.0060% ~ 0.0180%, P = 0.040%, S = 0.040%, V:0.010% ~ 0.100%, Nb:0.010% ~ 0.030%, Cr:0.10% ~ 0.60%, the rest is Fe and inevitable impurities. The key of the preparation method is to feed the core line containing N after refining the LF furnace and adjust the N to the appropriate level. The method has the advantages of simple operation, high and stable nitrogen recovery rate, and can effectively reduce production cost, and is worth popularizing.
【技术实现步骤摘要】
含V、Nb、Cr微合金建筑钢棒材及其LF炉生产方法
本专利技术属于钢铁冶金领域,具体涉及一种含V、Nb、Cr微合金建筑钢棒材及其LF炉生产方法。
技术介绍
微合金钢主要是指在钢中添加很少量或者是微量的某种元素就能明显提高性能的钢,特别是提高钢的强度指标。现有技术条件下微合金钢主要通常添加很少量或者是微量钒、铌和钛而得到。微合金化的作用机制是:作为微量元素的钒、铌和钛加入钢液后,与钢液中的碳和氮结合,形成碳、氮的化合物质点,即V(C、N),Nb(C、N)和Ti(C、N)质点,这些质点具有一定的沉淀强化和晶粒细化的作用,可明显的提高钢的强度。由此可看出,实际上微合金钢钒、铌和钛的作用均是和氮分不开的,但一般情况下采用转炉冶炼钢,残留氮含量在0.0030%~0.065%范围内,采用电炉冶炼钢,残留氮含量在0.050%~0.085%范围内,大多数情况下。如要充分发挥钒、铌和钛的作用,是必须要额外加入氮元素才能实现的。早期在微合金钢中增加氮,是通过添加3%~6%的氮化类合金来实现的,但由于氮化类合金含氮很低,造成合金加入量大,且收得率不稳定,逐渐被氮含量较高的氮化钒合金代替。目前微合金钢的生产中几乎很难再使用3%~6%的氮化类合金,几乎全部使用即含钒、且氮含量又高的氮化钒合金。氮化钒合金主要有VN12、VN14和VN16三个牌号。一般情况下该三个牌号氮和钒的比值是基本固定的,分别为12:78(N:V);14:78(N:V);16:78(N:V),即氮和钒的比值最高为VN16的16:78,即合金中含有16%的N,含有78%钒。氮化钒合金虽然既含钒、且氮含量又高,但对于 ...
【技术保护点】
含V、Nb、Cr微合金建筑钢棒材,其特征在于,化学成分为:按重量百分比计,C:0.15%~0.30%、Si:0.30%~1.00%、Mn:0.60%~1.30%、N:0.0060%~0.0180%、P≤0.040%、S≤0.040%、V:0.010%~0.100%、Nb:0.010%~0.030%、Cr:0.10%~0.60%,余量为Fe和不可避免的杂质。
【技术特征摘要】
1.含V、Nb、Cr微合金建筑钢棒材,其特征在于,化学成分为:按重量百分比计,C:0.15%~0.30%、Si:0.30%~1.00%、Mn:0.60%~1.30%、N:0.0060%~0.0180%、P≤0.040%、S≤0.040%、V:0.010%~0.100%、Nb:0.010%~0.030%、Cr:0.10%~0.60%,余量为Fe和不可避免的杂质。2.权利要求1所述的含V、Nb、Cr微合金建筑钢棒材的LF炉生产方法,其特征在于,包括以下步骤:高炉铁水经转炉冶炼、LF精炼、连铸制得钢坯;钢坯经加热、连续式棒材轧制生产线轧制成材、冷却制成圆棒或带肋钢筋;其中LF炉精炼后在钢包内喂入包芯线调整N,钢坯加热温度控制为950~1220℃,均热温度控制为1000~1200℃,加热和均热总时间90~120min;所述钢坯成分为:按重量百分比计,,C:0.15%~0.30%、Si:0.30%~1.00%、Mn:0.60%~1.30%、N:0.0060%~0.0180%、P≤0.040%、S≤0.040%、V:0.010%~0.100%,Nb:0.010%~0.030%、Cr:0.10%~0.60%,余量为Fe和不可避免的杂质。3.根据权利要求2所述的含V、Nb、Cr微合金建筑钢棒材的LF炉生产方法,其特征在于,包括以下步骤:a、转炉冶炼在转炉内加入铁水和废钢,利用转炉吹氧脱C,进行冶炼,待钢水C含量为0.05%~0.15%,P含量≤0.025%、S含量≤0.035%,钢水温度≥1650℃时出钢;出钢1/3-2/3时,加入FeSi、FeMn、FeCr、FeNb合金和增碳剂,FeV或VN合金,控制C为0.15%~0.30...
【专利技术属性】
技术研发人员:郭跃华,刘明,邓通武,赵志强,
申请(专利权)人:攀钢集团攀枝花钢铁研究院有限公司,
类型:发明
国别省市:四川,51