The invention discloses a method for preparing an adsorption of cobalt and copper beta naphthol modified activated carbon. (1) 50 80 DEG C temperature range, the beta naphthol dissolved in mass percentage concentration of 1 5% ethanol or sodium hydroxide solution, prepared into 0.1 beta naphthol 1mol/L mixed solution; (2) the 5 10g activated carbon into the 100mL step (1) mixed solution prepared in 10, immersion for 24 hours, and then filtered supernatant after drying, modified activated carbon preparation completed. The activated carbon prepared by the invention is a kind of special adsorbents to cobalt, copper ion adsorption and removal, simple preparation process, low cost, highly selective in the solution of copper or cobalt ion adsorption and removal, removal of cobalt ions can reach the limit below 0.5mg/L, copper ion limit below 0.1mg/L.
【技术实现步骤摘要】
吸附钴、铜离子的β-萘酚改性活性炭的制备方法
本专利技术涉及活性炭的改性和制备方法,特别是针对钴、铜离子的吸附、脱除用活性炭的开发利用。
技术介绍
活性炭作为一种吸附及催化材料,已在化工、石油、轻工、食品、环境保护、国防等诸多领域得到广泛应用。在环境保护、有色金属冶金、资源综合利用等领域的应用主要以活性炭对重金属离子的吸附性能为主要表现。在有色金属冶金和资源综合利用中,活性炭在低浓度溶液可以有效地对目标元素实施富集,在多元素共存溶液里能够吸附杂质离子实现除杂净化作用,因此活性炭已成为一些行业中特效的吸附剂或脱杂剂。大量的活性炭性质研究中发现,活性炭内部具有大量的官能团或基团,活性炭所表现出的一些催化或吸附性能取决于内在官能团或基团的性质,因此活性炭的改性或修饰研究方兴未艾,针对某种功能应用要求,可以有的放矢地对活性炭进行改性,从而实现活性炭对某些性能要求的目标。
技术实现思路
本专利技术的目的是为了制备一种高效选择性强的吸附用活性炭复合材料,通过添加活性剂的改性方法,制备出所需的活性炭。可以专门有效的吸附低浓度或多元素离子共存溶液中的铜、钴有价金属离子,是一种在环境保护、湿法冶金和资源综合利用领域具有高效、选择性强的吸附剂和除杂剂。具体步骤为:(1)50℃-80℃温度范围中,将β-萘酚溶于质量百分比浓度为1-5%的乙醇或氢氧化钠溶液中,配制成0.1-1mol/Lβ-萘酚混合溶液。(2)称取5-10g活性炭放入100mL步骤(1)所配制的混合溶液中,浸渍10-24小时,然后滤去清液后烘干,改性活性炭制取完成。(3)量取100mL浓度为0.5g/L的硫酸铜或硫酸钴 ...
【技术保护点】
一种吸附钴、铜离子的β‑萘酚改性活性炭的制备方法,其特征在于具体步骤为:(1)50℃‑80℃温度范围中,将β‑萘酚溶于质量百分比浓度为1‑5%的乙醇或氢氧化钠溶液中,配制成0.1‑1mol/Lβ‑萘酚混合溶液;(2)称取5‑10g活性炭放入100mL步骤(1)所配制的混合溶液中, 浸渍10‑24小时,然后滤去清液后烘干,改性活性炭制取完成。
【技术特征摘要】
1.一种吸附钴、铜离子的β-萘酚改性活性炭的制备方法,其特征在于具体步骤为:(1)50℃-80℃温度范围中,将β-萘酚溶于质量百分比浓度为1-5%的乙醇或氢氧化钠溶液中,配...