The invention discloses a modified electric appliance panel ABS alloy, which is characterized in that the weight of the material comprises the following: ABS resin 60-80, 1-3 enhancer, branched chain methyl phenyl siloxane prepolymer 10-15, modifier 1-6, pigment 1-2, maleic anhydride 1-5, zinc borate 10-15 10-15, polyvinyl ester, vinyl double stearic amide 15-17, stearic acid monoglyceride 2-4, three glycerin monostearate 1-8, polyethylene terephthalate, 5-9, polypropylene silicone monomer 1-8. The invention has the advantages that the method used in the blending process to add hardening enhancing agent, compatibilizer and flame retardant, improve the surface hardness of PC/ABS alloy, the PC/ABS improves the surface hardness and mechanical properties of flame retardant on the basis of little change to meet the technical requirements, so that the PC/ABS alloy is used more widely.
【技术实现步骤摘要】
一种改性电器产品面板ABS合金
本专利技术涉及一种改性电器产品面板ABS合金。
技术介绍
在PC/ABS合金合金广泛应用于电子电器产品的面板时，为了维持长久的外观美感和安全防火性能，对其表面硬度及阻燃性提出了新的要求。以往均是采用表面喷漆的方法提高表面硬度，但是其表面喷漆既增加成本且对环境保护造成一定的压力，为此，研究和开发高硬度的阻燃PC/ABS合金己显得十分重要。
技术实现思路
本专利技术所要解决的技术问题是提供一种改性电器产品面板ABS合金。为解决上述技术问题，本专利技术采用的技术方案是: 一种改性电器产品面板ABS合金，其特征在于，包括下列重量份数的物质:ABS树脂60-80份，增强剂1-3份，甲基苯基硅氧烷支链型预聚物10-15份，改性剂1_6份，颜料1_2份，马来酸酐1-5份，硼酸锌10-15份，聚乙烯酯10-15份，乙烯基双硬脂酰胺15-17份，硬脂酸单甘油酯2-4份，三硬脂酸甘油酯1-8份，聚对苯二甲酸乙酯5-9份，聚丙烯有机硅单体1-8份。本专利技术的有益效果是:其采用在共混过程中添加硬化增强剂、相容剂和阻燃剂的方法，对PC/ABS合金...
【技术保护点】
一种改性电器产品面板ABS合金，其特征在于，包括下列重量份数的物质：?ABS树脂60?80份，增强剂1?3份，甲基苯基硅氧烷支链型预聚物10?15份，改性剂1?6份，颜料1?2份，马来酸酐1?5份，硼酸锌10?15份，聚乙烯酯10?15份，乙烯基双硬脂酰胺15?17份，硬脂酸单甘油酯2?4份，三硬脂酸甘油酯1?8份，聚对苯二甲酸乙酯5?9份，聚丙烯有机硅单体1?8份。
【技术特征摘要】
1.一种改性电器产品面板ABS合金，其特征在于，包括下列重量份数的物质:ABS树脂60-80份，增强剂1-3份，甲基苯基硅氧烷支链型预聚物10-15份，改性剂1_6份，颜料1_2份，马来...