The invention discloses a medium temperature collector copper pipe welding protective gas and application by nitrogen and hydrogen mixed gas mixture, the weight percentage of the nitrogen in the mixed gas was 80% and the weight percentage of hydrogen is 20%, the use range of the mixed gas for back protection control of mixed gas in the welding of copper. In the welding process flow in 10~20L/min. This invention will be used as the nitrogen protective gas is replaced by a mixture of hydrogen and nitrogen, storage of raw material safety, process is simple to use, convenient operation, low cost, beautiful environment, can safely reduce the production cost saving nitrogen energy use, green environmental protection.
【技术实现步骤摘要】
一种中温集热器铜管焊接保护气体及应用
[0001 ] 本专利技术涉及一种焊接保护气体及应用,尤其涉及一种中温集热器铜调节器焊接保护气体及应用,属于焊接加工
。
技术介绍
目前,中温集热器作为太阳能系统收集热量的部件,市场需求量越来越大。一般集热器中铜调节器焊接过程中使用的保护气体多采用氮气,作为铜调节器加工过程中常用的保护气体,但是氮原子有较强的非金属性,在氮分子中有共价叁键,键能大,所以氮气化学性质不活泼。但在高温下,破坏了共价键,氮气可跟许多物质反应,焊接时的高温容易造成焊缝部位存留杂质,影响产品的焊接质量。
技术实现思路
本专利技术所要解决的技术问题是针对现有技术存在的缺陷,提供一种中温集热器铜管焊接保护气体及应用。 为解决这一技术问题,本专利技术提供了一种中温集热器铜管焊接保护气体,由氮气和氢气混合制得混合气体。所述混合气体中氮气的重量百分比为80%,氢气的重量百分比为20%。所述混合气体的使用范围为背面保护铜管焊接。在焊接过程中混合气体的流量控制在l(T20L/min。有益效果:本专利技术将用作保护性气体的氮气用氢氮混合气替代,原料储存安全、工艺使用简单、操作方便、生产成本低、生产环境优美,可以安全可靠地降低生产成本节约制氮所用能源,绿色环保。【具体实施方式】本专利技术由氮气和氢气按照氮气:氢气比例为80%:20%的比例将原料混合均匀,制得混合气体,用氢氮混合气替代保护性气体的氮气,这样可以安全可靠地降低生产成本节约制氮所用能源。按氮气:氢气为80%:20%的比例在铜管焊缝中进行保护,按GB/T26956-2011标准中的侵蚀 ...
【技术保护点】
一种中温集热器铜管焊接保护气体,其特征在于:由氮气和氢气混合制得混合气体,所述混合气体中氮气的重量百分比为80%,氢气的重量百分比为20%。
【技术特征摘要】
1.一种中温集热器铜管焊接保护气体,其特征在于:由氮气和氢气混合制得混合气体,所述混合气体中氮气的重量百分比为80%,氢气的重量百分比为20%。2.根据权利要求1所述的中温集热器铜管焊接保...