The invention relates to a process for producing copper sulfate by utilizing copper slag at normal temperature and pressure, belonging to the technical field of comprehensive recovery and utilization of non-ferrous metal smelting slag. The invention adopts room temperature (~ 25 degrees), atmospheric pressure (~ 1.01 * 105Pa) under the condition of copper containing 20 to 60% copper slag (other components containing Zn1 ~ 15%, Pb5 ~ 15%, Cd1 ~ 8%), grinding particle size reach -120 ~ -200 at present, and mixed acid containing 120 ~ 180g.L-1 sulfuric acid solution was added with stirring tank to tank into 0.05 ~ 0.5m3.min-1.Kg copper slag -1 (0.05 ~ 0.1Mpa) of the air, keep the tank sufficient oxidizing atmosphere. By using the heat released from the neutralization reaction between copper oxide and sulfuric acid, the oxidation reaction of copper and dilute sulfuric acid is promoted. After a sufficient reaction of 18 ~ 24h, copper can be leached into the solution better, and the leaching rate is over 94%.
【技术实现步骤摘要】
本专利技术是一种在常温常压下，利用铜 渣生产硫酸铜的工艺方法，属于有色金属冶 炼渣的综合回收利用
技术介绍
在锌的冶炼中，硫酸锌溶液净化过程需产出铜镉渣，铜镉渣再经过浸出，锌粉置换 得到海绵镉和铜渣，该铜渣部分氧化，铜渣一般含铜20 60% (其它成分为Znl 15%， Pb5 15%，Cdl 8% )。在现有的利用铜渣生产硫酸铜的技术中，一直认为铜渣中的铜主要以金属铜及少 量硫化铜形态存在，浸出之前须将铜渣氧化焙烧使金属态的铜和硫化铜转化成氧化铜，然 后再进行酸性浸出或强化浸出，浸出液经过除杂、净化、浓缩结晶后生产出硫酸铜产品。该 工艺存在流程长、生产能耗高、环境污染大、金属回收率低等问题。因此，开发一种节能环保的硫酸铜生产工艺，提升锌冶炼过程中有价金属的回收 具有十分重要的现实意义。
技术实现思路
本专利技术针对现有用铜渣生产硫酸铜技术中存在的问题，专利技术一种突破性的开发了 在常温常压下，利用铜渣生产硫酸铜的工艺方法。其流程短、能耗低、环境好、金属回收率高 的。本专利技术的目的上通过下列工艺步骤实现的(1)浸出以重量百分比计，在常温( 25°C ...
【技术保护点】
１．在常温常压下利用铜渣生产硫酸铜的工艺方法，其特征在于：（１）浸出：以重量百分比计，在常温（～２５℃）常压（～１．０１×１０５ｐａ）条件下，将含铜２０～６０％的铜渣合理磨矿粒度为－１２０～－２００目，与含酸１２０～１８０ｇ．Ｌ－１的硫酸溶液混合后加入带有机械搅拌的槽内，向槽内通入０．０５～０．５ｍ３．ｍｉｎ－１．Ｋｇ铜渣－１（０．０５～０．１Ｍｐａ）的空气，保持槽内充足的氧化气氛；通过利用氧化铜与硫酸中和反应放出的热量，促进铜与稀硫酸的氧化反应，在充分反应１８～２４ｈ，铜能较好地浸出到溶液中，其中铜渣的其它主要成分为：Ｚｎ１～１５％，Ｐｂ５～１５％，Ｃｄ１～８％；（２）澄...
【技术特征摘要】
【专利技术属性】
技术研发人员：雷德君，杨建斌，刘艳涛，段世卓，王建昆，钱万德，
申请(专利权)人：云南驰宏锌锗股份有限公司，
类型：发明
国别省市：53