铅酸蓄电池极板强化剂制造技术

一种铅酸蓄电池极板强化剂，由1.0～1.4％的氢氧化锂、0.6～1.0％的碳酸钠、0.06～0.1％的硫酸铋、0.4～0.6％的2，6-二叔丁基-4-甲基苯酚、0.1～0.3％的四硫磺酸钾以及余量为去离子水组成。本发明专利技术能在极板活性物质周围造成较好的弱碱环境，在充电电流的辅助下促使极板活性物质中α氧化铅高效率的生成，从而使极板得到强化。此外，本极板强化剂所含的铋等物质可以提高极板的孔率和导电性，从而增加蓄电池容量和循环寿命。

Lead-acid battery plate enhancer

A lead-acid battery polar enhancer, from 1 to 0.6 to 1.4% of lithium hydroxide, sodium carbonate, 1% ~ 0.06, 0.4 ~ 0.1% bismuth sulfate 0.6%, 2, four 6- sulfuric acid potassium tert butyl -4- methyl phenol, 0.1 ~ 0.3% and the remainder is composed of deionized water. The invention can make a better weak base environment around the active material of the polar plate, and under the assistance of the charging current, the alpha oxide of the polar plate active material can be efficiently generated, so that the polar plate is strengthened. In addition, the bismuth contained in the plate intensifier can improve the hole rate and conductivity of the polar plate, thereby increasing the storage capacity and the cycle life of the plate.

【技术实现步骤摘要】

本专利技术涉及一种铅酸蓄电池极板强化剂，属于蓄电池修复

技术介绍
铅酸蓄电池是指电极主要由铅及其氧化物制成，电解液是硫酸溶液的一种蓄电池。目前，铅酸蓄电池的用量巨大，但是其实际平均使用寿命还不到设计寿命的50%，比如通信基站用铅酸蓄电池设计浮充寿命一般为12年左右，实际有效使用寿命只有3 4年， 因此大量铅酸蓄电池过早地报废。这种情况产生的结果是两个一方面造成对土壤和水源的严重污染，另一方面造成巨大的经济浪费。铅酸蓄电池是利用化学反应来储蓄电能，而使用时将电能释放成化学物质的过程，每个铅酸蓄电池由浸泡于电解液(稀硫酸)的正极0 )与负极(Pb)构成，因化学反应在两极间产生电压，基本原理如下权利要求1. 一种铅酸蓄电池极板强化剂，其特征在于由下列质量百分含量的物质混合组成氢氧化锂1.0 ~ 1.4%;碳酸钠0.6-1.0%;疏酸铋0.06-0.1%;，2,6-二叔丁基-4-曱基苯酚0.4 ~ 0.6%;四硫磺酸钾0.1~0.3%; 去离子水余量。全文摘要一种铅酸蓄电池极板强化剂，由1.0～1.4％的氢氧化锂、0.6～1.0％的碳酸钠、0.06～0.1％的硫酸铋、0.4～本文档来自技高网...

【技术保护点】
１．一种铅酸蓄电池极板强化剂，其特征在于：由下列质量百分含量的物质混合组成：

【技术特征摘要】

【专利技术属性】
技术研发人员：陈玉涛，
申请(专利权)人：陈玉涛，
类型：发明
国别省市：32