The invention discloses a preparation method of an amphoteric ion polymer, which comprises the following steps: polyamine and chlorinated organic compounds according to the molar ratio of 1: 0.5 to 2.5 water mixing, mixing and dissolving, heating to 20 to 90 DEG C temperature reaction under atmospheric pressure; the pH value of reaction solution was decreased from 7 to 7.5 alkali, pH adjusted to 10 ~ 12, the end of reaction to the reaction to continue. The method of the invention is simple in process and easy to control, and the reagent is easy to purchase and the equipment needed is easy. Preparation of zwitterionic polymer prepared with high positive and negative ion charge, and because the polymer chains with crosslinkable hydroxy and tertiary amine groups on the H, it can be cross-linked subsequent by proper methods, such as the use of suspension reaction crosslinked amphoteric resin, the reaction can also be used as a membrane material existence in the absence of crosslinker was prepared containing zwitterionic membrane.
【技术实现步骤摘要】
本专利技术涉及，尤其涉及一种多乙烯多胺和含氯有机物为反应原料，通过亲核取代反应制备两性离子聚合物的方法。
技术介绍
两性离子聚合物同时携带正负两种离子电荷，即它的表面活性离子的亲水基既具有阴离子部分又具有阳离子部分。它在不同的PH值范围内可能携带不同性质的离子电荷，这使它们的分子之间、分子内存在相互吸引力和相互排斥力，因而有其他离子聚合物所不具备的性能。两性离子聚合物的合成方法主要有阴、阳离子单体的共聚、接枝共聚。目前研究较多的为两性聚丙烯酰胺的合成，对于两性聚丙烯酰胺的合成方法主要有水溶液聚合、反相乳液聚合和反相微乳液聚合等。如冉千平等在“两性高分子絮凝剂P(AM-DM-MA)的合成及性能评价”，油田化学，2002，19(1)中公开，在引发剂存在下使丙烯酰胺(AM)、二甲基二烯丙基氯化铵(DM)、马来酸(MA)在水溶液中共聚合，得到了两性共聚物P(AM/DM/MA)；杜翠鸣等在“两性聚合物的制备及其应用研究”，皮革科学与工程2007，17 (1)中公开，用阳离子单体二甲基二烯丙基氯化铵和丙烯酰氧乙基三甲基氯化铵分别与丙烯酰胺、丙烯酸通过溶液聚合制得两性聚合物P...
【技术保护点】
１．一种两性离子聚合物的制备方法，包括：将原料Ａ与含氯有机物按照摩尔比为１∶０．５～２．５混合，加水搅拌溶解后，在常压下升温至２０～９０℃恒温反应；反应溶液ｐＨ值下降至７．０～７．５时，加碱调节ｐＨ至１０～１２，继续反应至反应结束；所述的原料Ａ由结构式如式（１）所示且分子量大于１０００的多乙烯多胺混合组成；ｎ为自然数；所述的含氯有机物为含氯的有机磺酸盐。
【技术特征摘要】
【专利技术属性】
技术研发人员：吴春金，杜春慧，刘娜，姚燕红，王繁星，柏宏敏，钱阳扬，
申请(专利权)人：浙江工商大学，
类型：发明
国别省市：86