一种粉末多孔二氧化锰电极的制备方法技术

本发明专利技术公开了一种粉末多孔二氧化锰电极的制备方法，首先制备电解二氧化锰，然后称量一定质量的膨胀石墨及制备好的电解二氧化锰，将电解二氧化锰和膨胀石墨干混均匀，然后逐滴滴加羧甲基纤维素钠水溶液作为粘结剂，继续搅拌至获得膏状物体，将该膏体涂抹在钛网的两侧，经压实、烘干，即制得粉末多孔二氧化锰电极。本发明专利技术的粉末多孔二氧化锰电极的制备方法是一种易于实施、电极性能稳定、废水处理效率高的二氧化锰电极的制作方法。

Method for preparing powder porous manganese dioxide electrode

The invention discloses a method for preparing porous manganese dioxide electrode, the preparation of electrolytic manganese dioxide, electrolytic manganese dioxide and then expanded graphite and prepared some weighing the quality of the electrolytic manganese dioxide and graphite dry mixed evenly, then gradually drops with aqueous solution of sodium carboxymethyl cellulose as a binder, continue to stir to get paste, the paste on both sides of the titanium mesh, compacted, drying, preparing porous manganese dioxide electrode. The preparation method of the powder porous manganese dioxide electrode of the invention is a method for making manganese dioxide electrode with easy implementation, stable electrode performance and high waste water treatment efficiency.

【技术实现步骤摘要】

【技术保护点】
１．一种粉末多孔二氧化锰电极的制备方法，其特征在于，包含以下步骤：步骤１）电解二氧化锰的制备：采用钛合金做阳极、碳电极做阴极，硫酸锰作原料，硫酸锰的质量浓度为１３０～１５０ｇ／Ｌ，ｐＨ值为３．５～４．５，电解液温度为９０～９７℃，电流密度为８～２５ｍＡ／ｃｍ２，从阳极得到的沉积物经过洗涤、中和、研磨和烘干，即得到电解二氧化锰；步骤２）粉末多孔二氧化锰电极的制备：称取一定质量的膨胀石墨和经所述步骤１）制得的电解二氧化锰，二者的质量比为（１０～２０）∶（８０～９０），将电解二氧化锰和膨胀石墨干混均匀，然后逐滴滴加羧甲基纤维素钠水溶液作为粘结剂，继续搅拌至成膏状物体，将该膏体涂抹在钛网的两侧，经压实...

【技术特征摘要】

【专利技术属性】
技术研发人员：王东田，魏杰，黄勇，冯磊，郝晓丹，
申请(专利权)人：苏州科技学院，
类型：发明
国别省市：32