The present invention provides a high wear self-healing rubber handle plastic coating, the coating comprises a main agent, diluent and curing agent, the main agent of various components including the following parts by weight: two-component polyurethane resin A? 15-17.5, a two-component polyurethane resin, a B:15-17.5 concentration of 10% driers solution: 5-10, 6-7.5, Matt: leveling agent: 0.5-1, epoxy modified polysiloxane: 0-2, ethyl acetate, butyl acetate: 15-20: 15-20: 10-15, toluene. The invention also provides a preparation method of the coating and construction method, coating the coating for ABS, ABS+PC, HIPS and other plastic casing, it has good rubber handle at the same time, still has the characteristics of high resistance RCA ordinary rubber coating does not have, can be widely used in 3C and automotive interior products the plastic coating, with good appearance and touch effect, and also has the advantages of low toxicity, low pollution, low emission of VOC, in compliance with international environmental requirements.
【技术实现步骤摘要】
本专利技术申请涉及一种，属于 化工涂料
技术介绍
手感漆又称橡胶漆、弹性漆，喷涂于物体表面，呈 光或半 光状态，手感相当细 腻、平滑，外观雅致、庄重，耐划性、耐侯性、耐磨性优良。底漆是油漆系统的第一层，用于提高面漆的附着力、增加面漆的丰满度、提供抗碱 性、提供防腐功能等，同时可以保证面漆的均勻吸收，使油漆系统发挥最佳效果。面漆与底 漆的功能不同，面漆更加侧重于最终的装饰与表观效果，而底漆则侧重于提高附着力、防腐 功能、抗碱性等。3c产品塑料外壳进行弹性手感涂料目前流行于塑料产品加工商，但目前令众多涂 料供应商和塑料外观加工商头疼的问题经常是良好的橡胶触感和优良的涂料性能两者不 可兼得。不少厂商为了增强涂料的耐RCA性能的方法，经常是提高固化剂的配套比例，这 虽然能够使弹性手感涂料的耐磨性能得到提高，但却是以损失良好的橡胶弹性触感为前提 的。
技术实现思路
本专利技术的目的是提供一种高耐磨可自愈橡胶手感塑胶涂料，该涂料可解决良好的 橡胶触感和优良的涂料性能两者不可兼得的问题，并且满足该涂料适用期不小于4小时与 干燥条件(70°C χ 30-60分钟，室温时效...
【技术保护点】
１．一种高耐磨可自愈橡胶手感塑胶涂料，包括主剂、稀释剂和固化剂，其特征在于：所述主剂包括以下重量份的各种成分：１）双组份聚氨酯树脂Ａ １５－１７．５份；２）双组份聚氨酯树脂Ｂ １５－１７．５份；３）浓度为１０％的催干剂溶液 ５－１０份；４）哑粉 ６－７．５份；５）流平剂 ０．５－１份；６）环氧改性聚硅氧烷 ０－２份；７）醋酸乙酯 １５－２０份；８）醋酸丁酯 １５－２０份；９）甲苯 １０－１５份。
【技术特征摘要】
【专利技术属性】
技术研发人员：黄杰良，吴小浩，
申请(专利权)人：深圳市嘉卓成科技发展有限公司，
类型：发明
国别省市：94
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。