The invention relates to a novel method for continuous dissolution spinning of ultrahigh molecular weight polyethylene, which belongs to the technical field of polymer material preparation. Ultra high molecular weight polyethylene powder in the appropriate solvent by moderately high shear release of macromolecular tangles, form a uniform emulsion mixture, then the emulsion mixture through the material storage tank stirring quantitative feeding screw extruder, extrusion to form a transparent solution are mixed output one, through the filter, into the box metering pump is measured from the spinneret hole nozzle, and then treated with a water bath extraction, drying, ultra drawing, have high strength and high modulus fiber. The invention saves time and labor cost, it can dissolve the molecular weight of polymer million and above, the nominal concentration of ultra high molecular weight polyethylene and solvent for 150% (quality), dissolved more evenly.
【技术实现步骤摘要】
连续溶解超高分子量聚合物的纺丝新方法。本专利技术涉及一种超高分子量聚 乙烯连续溶解纺丝新方法。超高分子量聚乙烯冻胶紡丝一超拉伸技术制备高强度、高模量聚乙稀纤维自荷兰DSM公司于1979年申请专利，目前己在荷兰、日本、美国、中国都实 现了工业化生产。并各自取得了生产超高分子量聚乙烯纤维的工艺专利。超高分子量聚乙烯冻胶纺丝主要步骤简叙如下将超高分子量聚乙烯加入 合适的溶剂中搅拌溶解制成溶液，溶液由螺杆挤压机挤出，经喷丝孔成型，然 后冷却、萃取、干燥超倍拉伸，最终获得成品纤维。其中得到溶解均匀的高聚 物溶液是关键。超高分子的尺寸庞大，大分子之间存在相互缠结可提高纤维的 可拉伸倍率得到高取向，使纤维达到高强度高模量。纤维的强度和模量随聚合 体的分子质量提高而增加。但是高聚物中过多而强的大分子间缠结引起的各种 粘弹性效果使得溶解变得复杂得多，缠结引起的粘弹性在搅拌时会产生韦森堡 效应(爬杆现象)。随着分子量的增加、聚合物浓度的提高和搅拌速度的加快， 韦森堡效应愈专利技术显，要制成均匀的溶液愈加困难。高聚物样品和低分子溶剂两 者间分子量相差悬殊。高分子链很长，不易移动。高分子...
【技术保护点】
一种超高分子量聚乙烯连续溶解纺丝新方法其包括：将超高分子量聚乙烯粉末在适当的溶剂中在解缠釜内，氮气保护下通过高剪切适度解除大分子间的缠结，形成均一乳液状混和液，然后乳液状混和液在常压下通过储料罐边搅拌边定量喂入螺杆挤出机，通过混合输送器，形成透明均一的溶液，经过滤器、箱体到计量泵被计量后从喷丝孔喷出，然后入水浴经处理后萃取干燥超倍拉伸，得到高强度高模量的纤维、管材或膜。
【技术特征摘要】
【专利技术属性】
技术研发人员：胡盼盼，刘兆峰，
申请(专利权)人：胡盼盼，刘兆峰，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。