一种用回收低粘度涤纶丝制造中粘度ＰＥＴ切片的方法技术

本发明专利技术提供了一种通过对回收低粘度涤纶纤维或涤纶织物碎片经双螺杆挤出机熔融挤出过程中加入增粘扩链剂进行熔融扩链挤出反应制备中粘度ＰＥＴ切片的方法。本方法是以回收的低粘度涤纶纤维或涤纶织物碎片为原料，加入增粘扩链剂通过挤出机反应挤出后使ＰＥＴ粘度增加。通过改变加工条件和反应配比，可得到不同粘度的ＰＥＴ切片。本发明专利技术得到的产物可用于工业用丝如地毯、纺丝等，也可以作为纺织物的原料。

Method for producing medium viscosity PET slice by recovering low viscosity polyester yarn

The present invention provides a method based on low viscosity polyester or polyester fiber recycling fabric pieces by twin-screw extruder melt extrusion process of adding tackifying extender in extrusion melt chain extension reaction preparation in viscosity of PET chip. The method takes the recovered low viscosity polyester fiber or polyester fabric fragments as raw materials, and adds viscosity increasing chain extender to increase the viscosity of the PET after the extruder is reacted and extruded. By changing the processing conditions and reaction ratio, PET slices with different viscosities can be obtained. The products obtained by the invention can be used for industrial silk, such as carpets, spinning, etc., and can also be used as raw materials for textiles.

【技术实现步骤摘要】

本专利技术涉及对回收低粘度涤纶纤维或涤纶织物碎片进行加工获得中等粘度PET切片的方 法，具体地说是利用双螺杆挤出机对经密实化处理或后粉碎的低粘度涤纶纤维加入增粘扩链 剂后进行反应挤出提高其特性粘数的方法，可用于生产中高粘度PET纺丝切片。此处提到的 密实化处理指的是将回收后的PET在经过清洗和一定温度的加热使表面融化成团，形成2 20mm的球体，便于精确加料和提高产量。
技术介绍
PET(聚对苯二甲酸乙二酯，俗称涤纶)自1953年由杜邦公司实现工业化以来，由于其良好 的物理加工性能和大工业化生产带来的成本降低所体现出来的性价比优势，迅速取代了许多 化学纤维的其它品种，目前已成为合成纤维中产量最大的一族。自2003年以来，全球PET 的产能以年均9%左右的速度扩张，2005年产能已达到约四千多万吨，2008年中国的产能已 超过2000万吨，己成为PET世界生产、消费第一大国。目前，世界上PET的主要使用在纤维和饮料包装瓶方面，特别是近些年来，PET瓶吹拉 技术、PET热灌装、亚热灌装技术，以及现在流行的PET冷无菌灌装技术，都推动了全球PET 瓶装饮料的蓬勃发展，PET在瓶料上的使本文档来自技高网...

【技术保护点】
一种用回收涤纶纤维或回收涤纶织物碎片（特性粘数从０．３５～０．５ｄｌ／ｇ）为原料，计量加入增粘扩链剂经双螺杆挤出机熔融混合、挤出、冷却成条、切粒后成为可用于纺丝的切片，该切片的特性粘数可从０．３５～０．５ｄｌ／ｇ提高至０．６－１．０ｄｌ／ｇ，可作为地毯、绳、线、服装面料等原料。其中挤出ＰＥＴ与增粘扩链剂的重量比为１００∶０．５～１０。

【技术特征摘要】