The invention relates to a sealing flat panel display substrate before and after pasting strip for the material by the following: first the composition by weight ratio of 70% to 90% PbO and 9% ~ 20% B: 2 O: 3 and 1% ~ 10% Bi: 2: O 3; second composition, which consists of 80 ~ 90% PbTlO: 3 and 10 ~ 20% Fe: 2 O: 3.Cr: 2 O: 3.1 / 2CoO and solvent composition. The invention also relates to the preparation method of the sticking strip. The front and back substrates of the display screen are sealed by the sticking strip of the invention, and the utility model has the advantages of simple operation and easy control of size.
【技术实现步骤摘要】
本专利技术涉及平板显示屏制造领域。具体地说，本专利技术涉及一 种用于封接平板显示屏前、后基板的贴敷条以及用于实现该方法的产品o
技术介绍
目前通用的交流气体i文电等离子显示屏(Plasma Display Panel, PDP)均采用表面放电型结构，包括一个前基板和与之封接 在一起的后基板，前基板上配置有透明电极ITO和汇流电极，透明 电极和汇流电极构成放电电极，；改电电极包括维持方文电电4及X和扫 描/维持放电电极Y，在放电电极的表面覆盖有一层介质层，介质层 上覆盖一层介质保护层。后基4反上配置有与方文电电4及相互垂直的寻 址电极，寻址电才及上覆盖一层介质层，介质层上配置有与其寻址电 极平行的条状障壁，且在条状障壁的底部覆盖有荧光粉层，前后基 板用〗氐熔点玻璃粉封^姿在一起，并且在其间充有Ne、 Ar、 Xe等的 混合》欠电气体。目前在等离子显示屏的制造过程中普遍应用低熔点玻璃粉作 为前基板与后基板之间进行密封的密封边封装层材料。封接方法大 多由机械手将封接用低熔点玻璃粉制成膏状浆料挤压于基板四边 加热熔封而成，也有采用丝网印刷方法，将^氐熔点3皮璃并分浆料通...
【技术保护点】
一种用于封接平板显示器基板的贴敷条，其特征在于，所述贴敷条由下列物质制成： 第一组合物，其由重量比７０％～９０％的ＰｂＯ、９％～２０％的Ｂ↓［２］Ｏ↓［３］和１％～１０％的Ｂｉ↓［２］Ｏ↓［３］组成； 第二组合物，其由８０～９０ ％的ＰｂＴｌＯ↓［３］和１０～２０％的Ｆｅ↓［２］Ｏ↓［３］.Ｃｒ↓［２］Ｏ↓［３］.１／２ＣｏＯ组成；以及溶剂。
【技术特征摘要】
1.一种用于封接平板显示器基板的贴敷条，其特征在于，所述贴敷条由下列物质制成第一组合物，其由重量比70％～90％的PbO、9％～20％的B2O3和1％～10％的Bi2O3组成；第二组合物，其由80～90％的PbTlO3和10～20％的Fe2O3·Cr2O3·1/2CoO组成；以及溶剂。2. 根据权利要求1所述的贴敷条，其中，所述溶剂选自由乙酸乙 面旨、乙酸丙酯、乙酸丁酯、和乙酸异戊酯构成的组。3. 根据权利要求2所述的贴敷条，其中，所述溶剂为乙酸异戊酯。4. 根据权利要求1所述的贴敷条，其中，所述第一组合物和第二 纟且合物的4吏用比例为5-7 : 4。5. 根据权利要求4所述的贴敷条，其中，所述第一组合物和第二 纟且合物的〗吏用比例为6 : 4。6. 根据权利要求1所述的方法，其中，所述溶剂与固体原料的重量比为1 : 11-12。7. 用于封接平板显示器基板的贴敷条的制作方法，包括以下步 ...
【专利技术属性】
技术研发人员：张小芳，唐翠珍，
申请(专利权)人：四川世纪双虹显示器件有限公司，
类型：发明
国别省市：11[中国|北京]