The invention relates to a composite powder for submerged arc surfacing of high boron alloy and its application method, which comprises the steps of dry mixing of powder components, wet mixing of mixed powder with pure water, rotary bonding granulation, low-temperature sintering, screening, etc. the composite powder of 6 mesh to 14 mesh is prefabricated in the weld bead, and the solid welding wire is used as the arc carrier for submerged arc surfacing to make the composite powder melt and the solid welding wire drop melt Integrated weld pool. Under the action of arc heat, most of the boron carbide and chromium components in the composite powder preferentially in-situ metallurgical reactions take place, forming the primary m with a maximum aspect ratio and a mean microhardness of 1622hv
【技术实现步骤摘要】
一种埋弧堆焊高硼合金的复合粉粒及其应用方法
本专利技术属于耐磨堆焊
，具体涉及一种埋弧堆焊高硼合金的复合粉粒及其应用方法。
技术介绍
高硼合金用作耐磨损零件材料，主要因其较为优异的耐磨粒磨损性能，由于硼在γ-Fe和α-Fe等基体的溶解度均低于0.02％，致使Fe2B等耐磨相易于析出，因而比同类高铬铸铁更为经济。高硼合金的制备方式有：砂型铸造、热扩渗和堆焊。砂型铸造可制备耐磨性能良好的硼合金，但铸件往往过厚、合金硼化物过脆，以及铸造熔体中硼和碳原子相互排斥而形成数量过多的共晶或者鱼骨状莱氏体等脆性相，致使铸造硼合金开裂敏感性大，可添加的硼、碳含量较为有限，多为亚共晶结构，这极大限制了其应用范围。热扩渗硼合金层厚度往往有限，只有0.06～0.32mm左右，磨粒磨损工况下服役期限短，且在外加载荷、腐蚀工况下易剥落；在低碳钢基体上堆焊高硼合金，其熔敷层所受拘束度小，可获得厚度更高和耐磨性良好的高硼合金，如低碳钢基体上药芯焊丝埋弧或自保护明弧堆焊高硼合金。但是，药芯焊丝的包粉量较为有限，硼组分添加量较为有限而压缩了其应用...
【技术保护点】
1.一种埋弧堆焊高硼合金的复合粉粒，采用粉末组分过筛称量、粉末组分干混、混合粉末添加纯净水湿混、旋转粘合造粒、低温烧结、筛分等步骤制成粒度6目～14目的复合粉粒；所述复合粉粒所含粉末组分的重量百分含量分别为：60～70%的含铬量99%以上的金属铬(Cr)；16～18%的碳化硼(B
【技术特征摘要】
1.一种埋弧堆焊高硼合金的复合粉粒，采用粉末组分过筛称量、粉末组分干混、混合粉末添加纯净水湿混、旋转粘合造粒、低温烧结、筛分等步骤制成粒度6目～14目的复合粉粒；所述复合粉粒所含粉末组分的重量百分含量分别为：60～70%的含铬量99%以上的金属铬(Cr)；16～18%的碳化硼(B4C)；5～7%的含硅量40～47%的硅铁(FeSi45)；4～6%的含锰量为78～85%、含碳量为1.5%的中碳锰铁(FeMn80C1.5)；1～2%的含铝量不低于99%的铝粉(Al)；3～5%的零水硅酸钠；余量为含铁量不低于98%的还原铁粉(Fe)。
2.根据权利要求1所述的一种埋弧堆焊高硼合金的复合粉粒，其特征在于：所述复合粉粒所含粉末组分中的金属铬、碳化硼、硅铁、中碳锰铁、还原铁粉的粉末过60目筛，铝粉过300目筛，零水硅酸钠的粉末过80目后称量。
3.根据权利要求1所述的一种埋弧堆焊高硼合金的复合粉粒，其特征在于：复合粉粒所含零水硅酸钠粉末组分的模数为1.0～1.4。
4.根据权利要求1所述的一种埋弧堆焊...