The invention discloses a preparation method for optimizing the properties of porous branched Pt \u2011 Ru \u2011 Ni alloy nanoparticles. In the invention, platinum acetylacetonate, ruthenium acetylacetonate and nickel acetylacetonate are used as metal precursors, oleamine is used as solvent, oleamine and oleic acid are used as surfactants, oleamine and formaldehyde are used as reducing agents, and the oven is used to assist in the synthesis of porous branched Pt \u2011 Ru \u2011 Ni alloy nanoparticles with high selectivity. This method is simple and repeatable, which enriches the design idea of Pt based alloy nanoparticles catalyst. The porous dendrite Pt \u2011 Ru \u2011 Ni alloy nanoparticles obtained have high specific surface area and large pore capacity, improve and increase the active sites and make full use of them, showing excellent durability and anti CO poisoning ability, and have a wide application prospect.
【技术实现步骤摘要】
一种优化多孔枝蔓状Pt-Ru-Ni合金纳米颗粒性能的制备方法
本专利技术属于功能纳米材料
具体的说，本专利技术是采用溶剂热合成法制备多孔枝蔓状Pt-Ru-Ni合金纳米粒子。
技术介绍
在过去的几十年里，环境问题日益突出、资源逐渐枯竭，对可再生燃料电池的需求已经迫在眉睫。由于甲醇燃料电池可再生，且具有能量转换效率高、污染物排放低等优点，使其成为最具有吸引力的电源。高性能、低成本的催化剂被认为是制约直接甲醇燃料电池广泛应用的关键。到目前为止，对甲醇氧化最有前途的阳极催化剂被认为是Pt。然而，Pt的高成本以及商业Pt基催化剂容易被甲醇氧化时产生的CO毒害，极大地限制了它的应用。因此提高Pt的利用率和抗中毒性能，提高Pt的催化活性迫在眉睫。大量的研究结果表明3d结构的过渡金属M与Pt构成的二元或者三元合金催化剂比纯Pt催化剂表现出了更高的催化活性和耐久性能。这是由于第二和第三金属的掺入会产生配体效应和应力效应，从而改变Pt原本的电子结构。此外，PtRu是最好的甲醇甲酸电氧化催化剂之一，但是由于PtRu是贵金属,昂贵的...
【技术保护点】
1.多孔枝蔓状Pt-Ru-Ni合金纳米颗粒的制备方法，具体步骤为：/n将Pt(acac)
【技术特征摘要】
1.多孔枝蔓状Pt-Ru-Ni合金纳米颗粒的制备方法，具体步骤为：
将Pt(acac)2，Ni(acac)2，Ru(acac)3，油胺和油酸加入烧杯中，然后将混合溶液超声10min，搅拌30min至溶液澄清；然后在搅拌状态下加入0.8ml甲醛，继续搅拌15min；将混合液转移到20ml的反应釜中，放入烘箱，在170℃下保持12h；反应结束后经过乙醇离心洗涤、冷冻干燥等处理步骤，得到多孔枝蔓状Pt-Ru-Ni合金纳米粒子。
2.权利要求1所述的多孔枝蔓状Pt-Ru...
【专利技术属性】
技术研发人员：李彬生，高道伟，杨绍寒，陈国柱，
申请(专利权)人：济南大学，
类型：发明
国别省市：山东;37