The invention belongs to the technical field of iron and steel metallurgy sintering, in particular to a composite additive and sinter for strengthening sintering process and a preparation method thereof. According to the weight percentage, the composite additive for strengthening sintering process of the invention is composed of 0.05% - 10% boron compound, 0.03% - 6% oxidant and 0.01% - 2% polyethylene glycol, and the rest is water, which is prepared according to the distribution ratio of each group After that, mix them evenly. This additive is mixed into the sinter mixture in a certain proportion, with a dosage of 0.5-2kg/t. It can be fully mixed for pelletizing, distributing, igniting and sintering in the sintering machine, which can effectively improve the sintering efficiency, improve the quality of sinter and strengthen the smelting of blast furnace.
【技术实现步骤摘要】
一种强化烧结过程的复合添加剂及烧结矿及其制备方法
本专利技术属于钢铁冶金烧结
，主要涉及一种强化烧结过程的复合添加剂及烧结矿及其制备方法。
技术介绍
铁矿烧结是目前国内外钢铁企业最广泛采用的含铁原料造块方法，为高炉提供具有一定粒度、强度且化学成分稳定的炉料。目前我国高炉炼铁的含铁炉料中75％以上为烧结矿，其需求量十分巨大，且烧结矿的技术指标将直接影响高炉冶炼的效果、生产成本和产品质量。影响烧结矿质量和产量的因素，除了与烧结矿的化学成分如烧结矿碱度、烧结矿品位、二氧化硅含量、氧化亚铁含量等有关之外，还与生产操作工艺以各阶段工艺操作技术水平和工艺参数有关，如混料的均匀性、水分的控制、预热、燃烧的速度与升温速度、熔融反应的温度及反应的介质、气氛以及冷凝过程中析出矿物的晶形控制等，都会影响烧结矿的产量和质量。如何有效地提高烧结矿的产量和质量，改善烧结矿的冶金性能，降低生产成本，一直是广大烧结和炼铁工程技术人员及专家关注和研究的课题。CN103215442A公开了一种厚料层烧结料面喷洒的覆盖剂及喷洒方法，该覆盖剂由碳精矿...
【技术保护点】
1.一种强化烧结过程的复合添加剂，其特征在于，按重量百分比计，其组成成分为：/n0.05％～10％含硼化合物，0.03％～6％氧化剂，0.01％～2％聚乙二醇，其余为水。/n
【技术特征摘要】
1.一种强化烧结过程的复合添加剂，其特征在于，按重量百分比计，其组成成分为：
0.05％～10％含硼化合物，0.03％～6％氧化剂，0.01％～2％聚乙二醇，其余为水。
2.根据权利要求1所述的一种强化烧结过程的复合添加剂，其特征在于，所述含硼化合物为四硼酸钾和四硼酸钠中的一种或两种的混合物。
3.根据权利要求1所述的一种强化烧结过程的复合添加剂，其特征在于，所述氧化剂为过硼酸钠和次氯酸钠中的一种或两种的混合物。
4.一种制备权利要求1-3任意一项所述强化烧结过程的复合添加剂的方法，其特征在于，包括如下过程：将含硼化合物、氧化、聚乙二醇和水混合均匀，得到所述复合添加剂。
5.一种烧结矿，其特征在于，其原料中添加有权利要求1-3任意一项...