The invention discloses a nano wood plastic composite board material, which is composed of PVC, natural fiber, inorganic nano particle, SiC nano powder and various auxiliaries; the weight ratio is: pvc40-50%, natural fiber 20-30%, inorganic nano particle 3-5%, SiC nano powder 5-8%, various auxiliaries 10-15%; the natural fiber is wood powder; glycol / coupling treatment (silane and titanium) is adopted Acid ester (AAS) composite process is used to pretreat wood powder fiber; further improvement is that inorganic nano particles are montmorillonite particles, calcium carbonate particles, silica particles, kaolin particles, talc particles, titanium dioxide particles, carbon black or their two or more mixtures. The invention can realize the full utilization of wood scraps and waste materials, the compatibility between wood powder and PVC base material is good, and the strength and toughness are high.
【技术实现步骤摘要】
纳米木塑复合板料
本专利技术涉及一种高分子复合材料，特别是一种纳米木塑复合板料。
技术介绍
随着我国国民经济的高速发展和人民生活水平的提高，人们对木材的需求量日益增加，而天然的林业发展速度远远跟不上市场对木材的需求，为了缓解木材的供求矛盾，各地相继出现了许多塑料和木塑材料，用以代替木材，但现有木塑材料的主要缺陷在于：木粉与PVC基材之间的相容性差，所以木粉用量比较少。
技术实现思路
本专利技术针对现有技术的不足，提出一种显著改善木粉与PVC基材之间相容性的纳米木塑复合板料。本专利技术通过下述技术方案实现技术目标。纳米木塑复合板料，由PVC、天然纤维、无机纳米粒子、SiC纳米粉末和各种助剂组成；其改进之处在于：重量配比为：PVC40～50％，天然纤维20～30％，无机纳米粒子3-5％，SiC纳米粉末5-8％，各种助剂10-15％；所述天然纤维为木粉；采用乙二醇/偶联处理（硅烷和钛酸酯，AAS）复合工艺，对木粉纤维进行预处理。进一步改进在于：无机纳米粒子为蒙脱土粒子、碳酸钙粒子、二氧化硅粒子、高龄土粒子、滑石粉粒子、钛白粉粒子、炭黑或它们两种或两种以上的混合物。本专利技术与现有技术相比，具有以下积极效果：1、天然纤维为木粉，实现木材边角料、废料的充分利用，节省木材资源。2、加入SiC纳米粉末，增加复合材料的强度和耐磨性。3、采用乙二醇/偶联处理（硅烷和钛酸酯，AAS）复合工艺，对木粉纤维进行预处理，改善了木粉、秸杆等天然纤维与PVC基材间的相容性...
【技术保护点】
1.一种纳米木塑复合板料，由PVC、天然纤维、无机纳米粒子、SiC纳米粉末和各种助剂组成；其特征在于：重量配比为：PVC40～50％，天然纤维20～30％，无机纳米粒子3-5％，SiC纳米粉末5-8％，各种助剂10-15％；所述天然纤维为木粉；采用乙二醇/偶联处理（硅烷和钛酸酯，AAS）复合工艺，对木粉纤维进行预处理。/n
【技术特征摘要】
1.一种纳米木塑复合板料，由PVC、天然纤维、无机纳米粒子、SiC纳米粉末和各种助剂组成；其特征在于：重量配比为：PVC40～50％，天然纤维20～30％，无机纳米粒子3-5％，SiC纳米粉末5-8％，各种助剂10-15％；所述天然纤维为木粉；采用乙二醇/偶联...
【专利技术属性】
技术研发人员：袁俊，
申请(专利权)人：泰州市华丽塑料有限公司，
类型：发明
国别省市：江苏;32