The invention discloses an environment friendly composite board, which is prepared by mixing waste plastics, natural fiber, plastic compatibilizer, silane coupling agent, filler, auxiliary agent and the like. The invention of manufacture of composite plate by adding wood powder, straw, chaff and other natural fiber and waste plastic, wood powder and straw, rice husk fiber and other agricultural wastes containing more cellulose, the tensile strength and elongation at break of composite material has the advantages, is conducive to improve the tensile properties of composite sheet. At the same time, some additives and fillers are added to improve the comprehensive properties of the composite sheet.
【技术实现步骤摘要】
一种环保型复合板材
本专利技术涉及材料领域,具体涉及一种环保型复合板材。
技术介绍
目前,利用木粉填充的塑料制品已应用于建材、家具、包装材料、装饰材料等领域,特别是近年来从环境友好角度出发,减少木材的使用,采用木粉填充制成复合塑料制品的市场越来越大。近些年,许多学者研究将非木天然纤维和废旧塑料与树脂复合,希望充分废弃物天然纤维且尽量不降低复合材料的性能。
技术实现思路
本专利技术目的在于,提供一种环保型的复合板材,本专利技术采用的技术方案如下:一种环保型复合板材,其特征在于,由以下组分按重量百分比混合制备而成:废旧塑料20-50份天然纤维20-50份塑料相容剂2-5份硅烷偶联剂1-3份填料5-15份助剂1-5份。进一步地,所述的废旧塑料主要成份为高密度聚乙烯。进一步地,所述的天然纤维是由木粉,谷壳,秸秆混合组成。进一步地,所述的天然纤维经过剥离破碎以及表面偶联处理,长度分散在1-5mm。进一步地,所述的填料是由碳酸钙,600-800目滑石粉,气相二氧化硅混合组成。进一步地,所述的助剂包括润滑剂,脱模剂,改性剂,增强剂。本专利技术相对于现有技术的有益效果是:本专利技术通过添加木粉、秸秆、谷壳等天然纤维与废旧塑料进行复合制备复合板材,木粉与秸秆、谷壳的纤维等农业废弃物含有更多的纤维素,使得复合板材的拉伸强度与断裂伸长率都具有优势,有利于提高复合板材的拉伸性能。同时添加适量的助剂以及填料大大提高了复合板材的综合性能。具体实施方式以下将结合实施例对本专利技术的构思及产生的技术效果进行清楚、完整地描述,以充分地理解本专利技术的目的、特征和效果。显然,所描述的实施例只是本 ...
【技术保护点】
一种环保型复合板材,其特征在于,由以下组分按重量百分比混合制备而成:废旧塑料 20‑50份天然纤维 20‑50份塑料相容剂 2‑5份硅烷偶联剂 1‑3份填料 5‑15 份助剂 1‑5份。
【技术特征摘要】
1.一种环保型复合板材,其特征在于,由以下组分按重量百分比混合制备而成:废旧塑料20-50份天然纤维20-50份塑料相容剂2-5份硅烷偶联剂1-3份填料5-15份助剂1-5份。2.根据权利要求1所述的环保型复合板材,其特征在于,所述的废旧塑料主要成份为高密度聚乙烯。3.根据权利要求1所述的环保型复合板材,其特征在于,所述的天然纤维是由木粉,谷壳,秸...