本发明专利技术的目的在于提供一种满足编织袋胶黏性能的同时能延长编织袋使用寿命的胶黏剂的制备方法。添加有天然橡胶乳，天然橡胶最大的特点是胶黏性强，韧性强，环境友好，应用广泛，添加天然胶乳能增加胶黏剂的胶黏性和抗老化性能，延长编织袋的使用寿命，添加的甲基丙烯酸丙酯能增加编织袋的耐磨性能。

A preparation method of water resistant and wear resistant adhesive for woven bags

The purpose of the invention is to provide a preparation method of the adhesive which can meet the adhesive performance of the woven bag and extend the service life of the woven bag. Adding natural rubber latex, the greatest characteristics of natural rubber are strong adhesiveness, toughness, environmental friendliness and wide application. Adding natural latex can increase the adhesive and anti-aging properties of adhesive, prolong the service life of woven bags, and the addition of propyl methacrylate can increase the wear resistance of woven bags.

【技术实现步骤摘要】
一种阻水高耐磨编织袋胶黏剂的制备方法
本专利技术涉及到一种阻水高耐磨编织袋胶黏剂的制备方法，属于编织袋制造

技术介绍
目前，编织袋是分为编织袋本体、胶黏层、薄膜三层的分层结构，其中胶黏层是用胶黏剂将编织袋本体和薄膜层粘合在一起。在编织袋复合编织袋袋口采用卷边后棉线缝包的封口工艺，三层材料复合和袋口卷边棉线缝包封口的目的是为了起到防水、防湿、防霉和防虫的作用，使谷物粮食保鲜和长期保存。但是，传统的粘合层，粘性较差，长期使用后，会出现薄膜层与复合编织袋本体脱离的现象，且易老化，发黄。甲基丙烯酸丙酯一种无色、具有甜味和酯气味的易燃的液体，用作制造丙烯酸酯溶剂型和乳液型胶黏剂的软单体，其硬度是虽然没有甲基丙烯酸甲酯、甲基丙烯酸乙酯高，但是比甲基丙烯酸丁酯高，所以其耐磨性能较甲基丙烯酸丁酯更好。其低黏度聚合物可用作特种涂料、纸张及皮革加工助剂、胶黏剂等。其透明的特性可以在满足编织袋胶黏性能的同时，又能增加光线的透过性，使编织袋的印刷颜色亮丽鲜艳，增加编织袋的美观性。天然胶乳属于橡胶类的热塑性合成树脂，其特点是高弹性、粘接时成膜性本文档来自技高网...

【技术保护点】
1.一种阻水高耐磨编织袋胶黏剂的制备方法，其特征在于：所述制备方法具体如下：/n(1)将酚醛树脂胶黏剂加入水中，升温至60～75℃，搅拌至完全溶解，向溶液中添加氢氧化钠溶液将其pH调至6.5～7；/n(2)向溶液中加入桐油和环氧树脂，反应30～45min，将溶液降至室温，得到胶黏剂粗液；/n(3)向制备的胶黏剂粗液中加入甲基异丁酮，并搅拌均匀，在常温、压力为0.05～0.098MPa下进行挥发处理5～10min；/n(4)向挥发处理完成的溶液中加入天然橡胶、甲基丙烯酸丙酯、抗氧化剂及防老剂，在300r/min的搅拌速度下搅拌均匀，并得到糊状物；/n(5)将制备得到的糊状物利用热水洗涤3次，然后...

【技术特征摘要】
1.一种阻水高耐磨编织袋胶黏剂的制备方法，其特征在于：所述制备方法具体如下：
(1)将酚醛树脂胶黏剂加入水中，升温至60～75℃，搅拌至完全溶解，向溶液中添加氢氧化钠溶液将其pH调至6.5～7；
(2)向溶液中加入桐油和环氧树脂，反应30～45min，将溶液降至室温，得到胶黏剂粗液；
(3)向制备的胶黏剂粗液中加入甲基异丁酮，并搅拌均匀，在常温、压力为0.05～0.098MPa下进行挥发处理5～10min；
(4)向挥发处理完成的溶液中加入天然橡胶、甲...